- Tytuł:
- Production of $LaCaMnO_3$ Composite by Ball Milling
- Autorzy:
-
Gencer, H.
Cengiz, N.
Kolat, V.
Izgi, T.
Atalay, S. - Powiązania:
- https://bibliotekanauki.pl/articles/1207685.pdf
- Data publikacji:
- 2014-02
- Wydawca:
- Polska Akademia Nauk. Instytut Fizyki PAN
- Tematy:
-
81.20.Ev
75.47.Lx
75.30.Sg - Opis:
- $La_{0.67}Ca_{0.33}MnO_3$ perovskite-type manganite was synthesized by high-energy ball milling raw oxides of $La_2O_3$ (purity 99.9%), $CaCO_3$ (purity > 99%), and MnO (purity > 99%). The ratio of ball and powder weight was 10:1 and the rotating speed was set to 500 rpm. X-ray analysis indicated that $La_{0.67}Ca_{0.33}MnO_3$ single phase was formed completely when milling time is up to 4 h. The peak intensity of perovskite structure decreased and a hump-like peak appeared with further milling time. When the milling time is longer than 40 h, the perovskite structure disappeared and the amorphous phase was formed completely. Scanning electron microscopy picture of 24 h milled sample showed that the particle size generally varies in a broad range from nanometer scale to a few μm. The magnetic measurements showed that ball milling samples have an inhomogeneous magnetic state and exhibit spin-glass like behavior. The significantly small magnetic entropy change and a remarkably broad temperature interval in entropy change were attributed to high degree of structural and magnetic disorder and broadening of magnetic transition.
- Źródło:
-
Acta Physica Polonica A; 2014, 125, 2; 214-216
0587-4246
1898-794X - Pojawia się w:
- Acta Physica Polonica A
- Dostawca treści:
- Biblioteka Nauki
Artykuł