Tytuł:: Anodic Oxide Coatings on Aluminium Resistant to Strong Alkali Environment
Autorzy:: Kozik, A.
Nowak, M.
Gędłek, K.
Leśniak, D.
Zasadziński, J.
Jurczak, H.
Powiązania:: https://bibliotekanauki.pl/articles/355544.pdf
Data publikacji:: 2019
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: anodic coating
sealing of anodic coatings
resistant to strong alkali environment
sealing quality
aluminium alloys
Opis:: The aim of this paper was to test currently available on the market products for sealing anodic oxide coatings as well as to test the use of other alternative substances improving the sealing process. The ability to seal in 10 different solutions and the quality of the seal has been tested. The influence of the applied preparations on corrosion resistance and resistance to strongly alkaline environment was also investigated. Based on the results obtained, satisfactory results were archived for the sample sealed in a IMN-OML (Institute of Non-Ferrous Metals in Gliwice, Light Metals Division) solution sealant and in solution of nickel acetate in a medium-temperature process. Sealing by means of nickel acetate solutions is economically justified, and its use allows the process temperature to be lowered. When it comes to resistance to alkalis, samples sealed in IMN-OML sealant are the best. Commercial solutions have also achieved positive results in all tests.
Źródło:: Archives of Metallurgy and Materials; 2019, 64, 4; 1335-1342
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Composite layers with ceramic matrix modified with glassy carbon destined for oil-less sliding pairings
Warstwy kompozytowe z osnową ceramiczną modyfikowane węglem szklistym przeznaczone na skojarzenia bezolejowe
Autorzy:: Posmyk, A.
Wistuba, H.
Powiązania:: https://bibliotekanauki.pl/articles/352687.pdf
Data publikacji:: 2011
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: warstwa kompozytowa
nanorurki węglowe
smarowanie
anodowa powłoka twarda
composite layer
carbon nanotubes
sliding
lubrication
anodic hard coating
Opis:: The paper presents basic knowledge about producing and some results of tribological and metallographical research on composite layers with porous, anodic hard coating matrix which were modified with glassy carbon nanotubes. These composite layers were formed as surface layers of machine parts operating under conditions of sparse lubrication (limited lubrication) and friction in air. The layers were tested at sliding mating with EN-GJL-350 cast iron used for piston rings in combustion engines and air compressors. On the basis of the metallographical tests was the structure of the composite layer described. It was fount that on the surface of the oxide is a glassy carbon layer and in the pores of oxide are regullary carbon nanotubes. On the basis of the obtained results of tribological tests it was found that glassy carbon layer on the oxide surface shorts the wering-in time, and the glassy carbon nanotubes formed inside the pores of anodic hard coating upon EN-AW-6061 aluminum alloy prove to be effective solid lubricants and complement lubrication function of the graphite in cast iron. Consequently the coefficient of friction was lower than in case of nanotubes-free oxide layers.
W pracy przedstawiono podstawy wytwarzania oraz wyniki badan metalograficznych i tribologicznych warstw kompozytowych na osnowie porowatej, anodowej warstwy tlenkowej modyfikowanej weglem szklistym. Warstwy te zostały wytworzone jako warstwy powierzchniowe czesci maszyn współpracujacych slizgowo w warunkach ograniczonego smarowania (oszczednego) oraz w warunkach tarcia technicznie suchego. Warstwy te zostały przebadane we współpracy slizgowej z zeliwem EN GJL 350 uzywanym na pierscienie tłokowe silników spalinowych i tłokowych sprezarek powietrza. Na podstawie przeprowadzonych badan metalograficznych okreslono budowe i strukture warstw kompozytowych, stwierdzajac ze na powierzchni tlenku wytwarza sie warstewka wegla szklistego, a wewnatrz porów sa regularne nanorurki weglowe. Na podstawie badan tribologicznych stwierdzono, ze znajdujaca sie na powierzchni warstewka wegla szklistego skraca czas docierania skojarzenia a nanorurki weglowe wytworzone w porach anodowej warstwy tlenkowej na stopie aluminium EN-AW-6061 sa skutecznym srodkiem smarowym i wspomagaja funkcje smarne grafitu znajdujacego sie w zeliwie. Współczynnik tarcia w skojarzeniu z warstwa kompozytowa był mniejszy niz w skojarzeniu z warstwa tlenkowa.
Źródło:: Archives of Metallurgy and Materials; 2011, 56, 4; 909-917
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "anodic coating" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język