Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "Ni-20Al" wg kryterium: Temat

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-4 z 4
    Tytuł:
    Effect of Isothermal Treatment on Ni3Al Coatings Deposited by Air Plasma Spraying System
    Autorzy:
    Mehmood, K.
    Rafiq, M. A.
    Durrani, Y. A.
    Khan, A. N.
    Powiązania:
    https://bibliotekanauki.pl/articles/354178.pdf
    Data publikacji:
    2018
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    air plasma spraying
    Ni-20Al
    residual stresses
    intermetallic coating
    nickel aluminide
    Opis:
    Ni3Al coatings were obtained on AISI 321 steel samples by air plasma spraying system. The behavior of heat treatment on intermetallic coatings were evaluated after exposure at various temperatures i.e. 500ºC to 800ºC. The stay time in this regard was varied from 10 to 100 hours. The coatings were then characterized by X-Ray diffraction analysis, optical and scanning electron microscopy, eddy current measurements and stress analysis. It was observed that the formation of NiO increases drastically with time and temperature. The hardness of the coating increases with the formation of NiO. It was noted that the residual stresses can be correlated with the formation of NiO. Further, the development of residual stresses can be monitored by a non-destructive technique i.e. eddy current method.
    Źródło:
    Archives of Metallurgy and Materials; 2018, 63, 1; 277-283
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Primary Microstructure Characterization of As-Casted Co-20Ni-7Al-7W Superalloy
    Autorzy:
    Tomaszewska, A.
    Moskal, G.
    Mikuszewski, T.
    Junak, G.
    Płachta, A.
    Powiązania:
    https://bibliotekanauki.pl/articles/380968.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    new Co based superalloys
    Co20Ni7Al7W alloy
    primary microstructure
    induction melting
    nowe nadstopy oparte na Co
    stop Co20Ni7Al7W
    mikrostruktura pierwotna
    topienie indukcyjne
    Opis:
    The primary microstructure of new Co-based superalloy of Co-20Ni-7Al-7W (at.%) type was showed in this article. The alloy was manufactured by induction melting in vacuum furnaces. This alloy is a part of new group of high-temperature materials based on Co solid solution and strengthened by coherent L12 phase similar to Ni-based superalloys with γʹ phase. The final form of Coss/L12 microstructure is obtained after fully heat treatment included homogenization, solutionizing and aging processes. But first step of heat treatment thermal parameters determination is characterization of primary microstructure of alloys after casting process with special attentions on segregations of alloying elements in solid solution and presences of structural elements such as eutectic areas, and other phases precipitations. In analysed case the relatively high homogeneity of chemical composition was expected especially in the case of W distribution, what was confirmed be SEM/EDS analysis in dendritic and interdendritic areas.
    Źródło:
    Archives of Foundry Engineering; 2019, 3; 78-83
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Influence of Alloying Elements on the Microstructure and Selected High-Temperature Properties of New Cobalt-Based L12-Reinforced Superalloys
    Autorzy:
    Kierat, Milena
    Moskal, Grzegorz
    Zieliński, Adam
    Jung, Tymoteusz
    Powiązania:
    https://bibliotekanauki.pl/articles/2106594.pdf
    Data publikacji:
    2022
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    Co10Al5Mo2Nb
    Co20Ni10Al5Mo2Nb
    casting
    primary microstructure
    segregation
    dendrites
    Opis:
    The study investigated the primary structure of the new generation of superalloys based on Co-10Al-5Mo-2Nb and Co-20Ni-10Al-5Mo-2Nb cobalt. Research on a group of cobalt-based materials was initiated in 2006 by J. Sato [1]. These materials may replace nickel-based superalloys in the future due to their excellent properties at elevated temperatures relative to nickel-based superalloys. The primary microstructure characterisation of the Co-10Al-5Mo-2Nb and Co-20Ni-10Al-5Mo-2Nb alloy are the basic subject of this article. The Co-10Al-5Mo-2Nb and Co-20Ni-10Al-5Mo-2Nb alloy are tungsten free alloys of a new type with the final microstructure based on the Co-based solid solution L12 phase of the Co3(Al,Mo,Nb) type as a strengthened structural element. The analysed alloys were investigated in an as-cast state after a vacuum casting process applied on graphite moulds. The primary microstructure of the alloys and the chemical constituent of dendritic and interdendritic areas were analysed using light, scanning electron and transmission microscopy. Currently, nickel-strengthened γ’ phase steels are still unrivalled in aerospace applications, however, cobalt based superalloys are a response to their existing limitations, which do not allow maintaining the current rate of development of aircraft engines.
    Źródło:
    Archives of Metallurgy and Materials; 2022, 67, 2; 495--500
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    D-gun Sprayed Fe-Al Single Particle Solidification
    Krystalizacja pojedynczej cząstki Fe-Al naniesionej metodą detonacyjną
    Autorzy:
    Wołczyński, W.
    Senderowski, C.
    Morgiel, J.
    Garzeł, G.
    Powiązania:
    https://bibliotekanauki.pl/articles/352240.pdf
    Data publikacji:
    2014
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    Fe-Al coating
    Ni-20Cr interlayer
    rapid solidification
    D-gun spraying
    boron localization
    competitive growth of phases
    powłoki FeAl
    międzywarstwy Ni-20Cr
    szybkie krzepnięcie
    metoda detonacyjna
    lokalizacja boru
    proces wzrostu faz
    Opis:
    Some Fe-Al particles less than 50 μm in diameter were deposited onto the steel substrate by means of the D-gun spraying. A solidification mechanism of an individual particle is described. The particle subjected to the description contained nominally 63 at.% Al. The description was preceded by the TEM / SAED analysis of both the Fe-Al coating and Ni-20Cr interlayer. The whole number of the analyzed particles was partially melted during the deposition. The solidification products like: amorphous phase sub-layer, oscillatory sub-layer which contains two types lamellae distributed alternately and typically non-equilibrium phase sub-layer were revealed. In the micro scale, solidification was considered as a process which occurred in two directions: towards the substrate and towards the non-melted particle part. Both solidification processes underwent the positive thermal gradients. The boron addition was localized within the eutectic precipitates pushed and then rejected by the solid/liquid interface of the solidifying non-equilibrium phase. The proposed model is a general one and therefore can be applied to other systems ;description.
    Cząstki proszku Fe-Al niniejsze niż 50 μm w średnicy zostały osadzone detonacyjnie na podłożu stalowym. Opisuje się mechanizm krystalizacji pojedynczej cząstki. Cząstki poddane opisowi zawierały nominalnie 63 aL% Al. Opis poprzedzono badaniami struktury metodą TEM / SAED dotyczącymi zarówno powłoki Fe-Al jak i między warstwy Ni-20Cr. Wszystkie analizowane cząstki były częściowo nadtopione podczas osadzania. Zidentyfikowano produkty krystalizacji takie jak: podwarstwę amorficzną, podwarstwę oscylacyjną zawierającą periodycznie ułożone pły tki dwu faz oraz podwarstwę zawierającą fazę typowo nierównowagową. W mikroskali proces wzrostu faz jest analizowany jako zachodzący w dwu kierunkach: w stronę podłoża i w stronę niestopionej części cząstki. Obydwa procesy wzrostu zachodziły w obecności dodatniego gradientu temperatury. Bor dodany do powłoki został zlokalizowany w eutektyce odepchniętej przez front krystalizacji fazy typowo nierównowagowej. Proponowany model ma charakter ogólny i może być zastosowany do opisu innych systemów.
    Źródło:
    Archives of Metallurgy and Materials; 2014, 59, 1; 211-220
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-4 z 4

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies