- Tytuł:
- Evaluation of Heat Capacity and Resistance to Cyclic Oxidation of Nickel Superalloys
- Autorzy:
-
Przeliorz, R.
Binczyk, F.
Gradoń, P.
Góral, M.
Mikuszewski, T. - Powiązania:
- https://bibliotekanauki.pl/articles/381534.pdf
- Data publikacji:
- 2014
- Wydawca:
- Polska Akademia Nauk. Czytelnia Czasopism PAN
- Tematy:
-
foundry technology
nickel superalloys
heat resistance
DSC calorimeter
heat capacity
technologie odlewnicze
nadstop niklu
odporność na ciepło
DSC kalorymetru
pojemność cieplna - Opis:
- Paper presents the results of evaluation of heat resistance and specific heat capacity of MAR-M-200, MAR-M-247 and Rene 80 nickel superalloys. Heat resistance was evaluated using cyclic method. Every cycle included heating in 1100°C for 23 hours and cooling for 1hour in air. Microstructure of the scale was observed using electron microscope. Specific heat capacity was measured using DSC calorimeter. It was found that under conditions of cyclically changing temperature alloy MAR-M-247 exhibits highest heat resistance. Formed oxide scale is heterophasic mixture of alloying elements, under which an internal oxidation zone was present. MAR-M-200 alloy has higher specific heat capacity compared to MAR-M-247. For tested alloys in the temperature range from 550°C to 800°C precipitation processes (γ′, γ′′) are probably occurring, resulting in a sudden increase in the observed heat capacity.