Tytuł:
Effect of Bismuth and Rare Earth Elements on Graphite Structure in Different Section Thicknesses of Spheroidal Graphite Cast Iron Castings
Autorzy:
Glavas, Z.
Strkalj, A.
Maldini, K.
Kozina, F.
Powiązania:
https://bibliotekanauki.pl/articles/353810.pdf
Data publikacji:
2018
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
spheroidal graphite cast iron casting
graphite structure
bismuth
rare earth elements
microstructure
Opis:
Effects of additions of 0.00064, 0.001 and 0.0042 wt.% Bi on the graphite structure in the section thicknesses of 3, 12, 25, 38, 50, 75 and 100 mm of spheroidal graphite cast iron castings containing 2.11 wt.% Si and rare earth (RE) elements (Ce + La + Nd + Pr + Sm + Gd) in the range from 0.00297 to 0.00337 wt.% were analyzed in this paper. Addition of Bi was not necessary for obtaining high nodule count and nodularity higher than 80% in section thicknesses of 3, 12 and 25 mm. RE elements showed a beneficial effect on the nodule count and nodularity in these sections. Nodularity was below 80% in section thicknesses of 38, 50, 75 and 100 mm when Bi was not added. Detrimental effect of RE elements on graphite morphology in these sections was neutralized by adequate addition of Bi. Addition of 0.001 wt.% Bi (ratio of RE/Bi = 3.27) was enough to achieve nodularity above 80% in the section thickness of 38 mm. Nodularity was increased above 80% in section thicknesses of 50, 75 and 100 mm by addition of 0.0042 wt.% Bi (ratio of RE/Bi = 0.78). At the same time, Bi significantly increased the nodule count. Nodularity above 80% and the high nodule count in the section thicknesses of 75 and 100 mm were also achieved by using an external metallic chill in the mold. In this case, addition of Bi was not required.
Źródło:
Archives of Metallurgy and Materials; 2018, 63, 3; 1547-1553
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies