Corrosion behavior of ZrC particles reinforcement with Al-12Si composites by weight loss method using acidic media
Autorzy:
John, C. F.
Paul, R. C.
Singh, S. C. E.
Jacobjose, J.
Ramkumar, T.
Hikku, G. S.
Sharma, R. K.
Sengottuvel, P.
Powiązania:
https://bibliotekanauki.pl/articles/200059.pdf
Data publikacji:
2018
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
Al-Si-ZrC composites
powder metallurgy
weight loss method
corrosion rate
SEM
kompozyty Al-Si-ZrC
metalurgia proszków
metoda redukcji masy
szybkość korozji
Opis:
This paper aims to investigate the corrosion behavior of zirconium carbide (ZrC) reinforced Al – Si metal matrix composites (MMCs) in a mixture of acidic solution using weight loss method. The composites are prepared by powder metallurgy method. Al-12Si-xZrC composites containing 0, 5, and 10 weight percentage of ZrC particles are compacted in a die set assembly and sintered in an inert gas muffle furnace. The acidic solutions used for corrosion are 1 N HCl, 1 N H2SO4 and 1 N HNO3. The corrosion characteristics of Al-12Si-xZrC composites and the pure Al were experimentally evaluated. The corrosion test was carried out at different weight proportions of the samples in various concentrations of the acid such as 1 N HCl, 1 N H2SO4 and 1 N HNO3 for different exposure time (i.e., 24 h, 72 h, 144 h and 216 h), respectively. The results specified that corrosion rate of composites was lower than that of base metal Al under the corrosive atmosphere, regardless of exposure time and acidic solutions used as corrodents. Al-12Si-xZrC composites become more corrosion resistant as the ZrC content is increased. This is because of the development of stable oxide layer above the specimens. Scanning electron microscopy (SEM) confirms the degree of attack of acidic solution on the surface of the examined material.
Źródło:
Bulletin of the Polish Academy of Sciences. Technical Sciences; 2018, 66, 1; 9-16
0239-7528
Pojawia się w:
Bulletin of the Polish Academy of Sciences. Technical Sciences
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies