Tytuł:: Influence of Hot Pressing on the Microstructure of Multi-Layered Ti/Al Composites
Autorzy:: Kowalski, Wojciech
Paul, Henryk
Petrzak, Paweł
Maj, Łukasz
Mania, Izabela
Faryna, Marek
Powiązania:: https://bibliotekanauki.pl/articles/2049145.pdf
Data publikacji:: 2021
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: Ti/al multilayers
electron microscopy
impact test
Opis:: Metal-intermetallic layered (MIL) composites attract considerable attention due to their remarkable structural and ballistic performance. This study aimed to develop a Ti/Al-based multilayered MIL material by adding ceramic powders, since they can improve the composite’s impact resistance. To this end, an experiment was conducted which a stack of alternating Ti and al sheets bonded by hot pressing; Ti/Al multilayers containing additional layers of Al2O3 and SiC powders were also produced. The samples obtained were examined using electron microscopy techniques. The clads’ mechanical properties were investigated using a Charpy hammer. In the reaction zone, only one intermetallic phase occurred: the Al3Ti phase. The model with an additional Al2O3 layer showed the highest impact energy. none of the Ti/Al clads broke during the Charpy impact test, a result proving their high ductility.
Źródło:: Archives of Metallurgy and Materials; 2021, 66, 4; 1149-1156
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Evaluation of the temperature stability of a Cu/Ni multilayer
Ocena trwałości temperaturowej wielowarstwy Cu/Ni
Autorzy:: Kucharska, B.
Kulej, E.
Gwoździk, M.
Powiązania:: https://bibliotekanauki.pl/articles/354250.pdf
Data publikacji:: 2012
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: wielowarstwa Cu/Ni
trwałość
stabilność temperaturowa
Cu/Ni multilayers
X-ray diffraction
texture
atomic force microscopy (AFM)
Opis:: The article presents investigation results for a Cu/Ni multilayer as annealed in the temperature range of 40 ÷300 degree Celsjus The Cu/Ni multilayer with a Cu sublayer thickness of 2 nm and an Ni sublayer thickness of 6 nm was fabricated by the magnetron deposition technique. The X-ray structural analysis, XRD, was employed for examination. The characterization of the multilayer before and after the annealing process was done by the measurement of the texture for the Cu/Ni(111) plane, as well as by topography examination on an atomic force microscope (AFM). The state of the multilayer surface were observed using a scanning electron microscope. The thermal stability tests showed that the multilayer had undergone delamination at temperature of 300 degree Celsjus . Up to this temperature, the multilayer retained clear phase boundaries, as confirmed by the presence of satellite peaks in the diffraction patterns. The annealing operation caused structural changes in the multilayer, such as grain growth and an increase in roughness and texture.
W artykule zaprezentowano wyniki badan wielowarstwy Cu/Ni wygrzewanej w zakresie temperatur 40÷300 stopni Celsjusza. Wielowarstwę Cu/Ni, o grubości podwarstwy Cu równej 2 nm i grubości podwarstwy Ni wynoszącej 6 nm, wytworzono technika osadzania magnetronowego. Do badań zastosowano rentgenowską analizę strukturalna XRD. Charakterystyki wielowarstwy przed i po procesie wygrzewania dokonano poprzez pomiar tekstury dla płaszczyzny Cu/Ni(111) jak również badania topografii na mikroskopie sił atomowych Veeco. Stan powierzchni wielowarstwy badano przy użyciu elektronowego mikroskopu skaningowego Jeol. Badania stabilności temperaturowej wykazały, że wielowarstwa uległa delaminacji w temperaturze 300 stopni Celsjusza. Do tej temperatury wielowarstwa zachowała wyraźne granice międzyfazowe, co potwierdzone zostało obecnością pików satelickich na obrazach dyfrakcyjnych. Wygrzewanie wywołało zmiany strukturalne w wielowarstwie, tj. rozrost ziaren, zwiększenie chropowatości i tekstury.
Źródło:: Archives of Metallurgy and Materials; 2012, 57, 3; 671-677
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "multilayers" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język