Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "macro-" wg kryterium: Temat

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-3 z 3
    Tytuł:
    Characteristic Investigation of Macro Fiber Composite Structure Using FE Model
    Autorzy:
    Saravanan, M. P.
    Marimuthu, Krishnaswamy
    Jayabal, Kaliappan
    Powiązania:
    https://bibliotekanauki.pl/articles/2049129.pdf
    Data publikacji:
    2021
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    macro-fiber composite
    finite-element model
    piezoelectric composite
    ANSYS
    RVE method
    Opis:
    In this investigation, the effective mechanical, coupling and dielectric properties of Macro-fiber-composites (MFCs) consisting of piezorod-element constituents are determined using representative volume element method combined with finite element analysis. Experiments are conducted on piezo-bar-element MFCs to understand the applicability of the proposed approach which would later be extended to composites with modified geometric pattern. The longitudinal strains with respect to static deflections of beam and forced displacements under varying electrical loads are measured for the MFCs, and compared with the numerical simulations. Based on the good agreement from the result comparisons of piezo-bar-element MFCs, the effective material properties of piezo-rod-element MFCs are numerically determined based on the RVE approach.
    Źródło:
    Archives of Metallurgy and Materials; 2021, 66, 4; 1059-1066
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Nature of Segregation in the Steel Static and Brass Continuously Cast Ingots
    Autorzy:
    Wołczyński, W.
    Powiązania:
    https://bibliotekanauki.pl/articles/356511.pdf
    Data publikacji:
    2018
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    macro-segregation maps
    brass ingots morphology
    marginal stability criterion
    Growth Law for columnar structure
    formation
    Opis:
    Experimental observations of the steel morphology as well as measurements of the solutes concentration in the macro-scale were made on the basis of the vertical cut at the mid-depth of the 15-tons steel forging ingot serially produced in one of the steel plant in Poland. Experimental observations of the morphology accompanied by the measurements of the Peclet Number were also made on the cross-section of the continuously cast brass ingots serially produced in the copper / brass industry in Poland. The performed measurements allowed to work out some maps of the alloying elements segregation for the longitudinal section of the steel static ingot and a Growth Law for the columnar grains formation in the brass ingots. The marginal stability criterion has been applied to the last mentioned development / description. Some suggestions for the micro-segregation measurement mode in the columnar structure are derived.
    Źródło:
    Archives of Metallurgy and Materials; 2018, 63, 4; 1915-1922
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Cet in solidifying roll - thermal gradient field analysis
    KRT w krystalizującym walcu - analiza gradientowego pola temperatury
    Autorzy:
    Wołczyński, W.
    Guzik, E.
    Wajda, W.
    Jędrzejczyk, D.
    Kania, B.
    Kostrzewa, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/354553.pdf
    Data publikacji:
    2012
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    walec krystalizujący
    gradientowe pole temperatury
    transformacja CET
    makrosegregacja
    solidifying roll
    thermal gradient field
    columnar into equiaxed structure transition
    macro-segregation index
    Opis:
    As the first step of simulation, a temperature field for solidifying cast steel and cast iron roll was created. The convection in the liquid is not comprised since in the first approximation, the convection does not influence the analyzed occurrence of the C - E (columnar to equiaxed grains) transition (CET) in the roll. The obtained temperature field allows to study the dynamics of its behaviour observed in the middle of the mould thickness. This midpoint of the mould thickness was treated as an operating point for the C - E transition. A full accumulation of the heat in the mould was postulated for the C - E transition. Thus, a plateau at the T(t) curve was observed at the midpoint. The range of the plateau existence tC - tE corresponded to the real period of transition, that occurs in the solidifying roll. At the second step of simulation, the thermal gradients field was studied. Three ranges were distinguished: a/ for the formation of the columnar structure (the C - zone): The columnar structure formation was significantly slowed down during incubation period. It resulted from a competition between columnar growth and equiaxed growth expected at that period of time. The relationship was postulated to correspond well with the critical thermal gradient, Gcrit.. A simulation was performed for the cast steel and cast iron rolls solidifying as if in industrial condition. Since the incubation divides the roll into two zones (columnar and equiaxed) some experiments dealing with solidification were made on semi-industrial scale. A macrosegregation equation for both mentioned zones was formulated. It was based on a recent equation for redistribution after back-diffusion. The role of the back-diffusion parameter was emphasized as a factor responsible for the redistribution in columnar structure and equiaxed structure.
    W pierwszym etapie symulacji wygenerowano numerycznie pole temperatury dla krzepnącego walca staliwnego oraz żeliwnego. Nie uwzględniono konwekcji uznając, że w pierwszym przybliżeniu konwekcja nie wpływa na przebieg transformacji C - E (struktura kolumnowa w równoosiową, CET). Uzyskane pole temperatury pozwala na analizę jego zachowania w środku grubości wlewnicy. Ten punkt wlewnicy zostałpotraktowany jako punkt operacyjny dla transformacji C - E. Postuluje się w tym modelu, że zachodzi pełna akumulacja ciepła we wlewnicy właśnie dla tej transformacji. Stąd, spłaszczenie krzywej T(t) jest obserwowane dla punktu operacyjnego. Zakres tego spłaszczenia oznaczony tC - tE odpowiada rzeczywistemu okresowi transformacji, tRC - tRE który pojawia się w krzepnącym walcu. W drugim etapie symulacji analizuje się gradientowe pole temperatury. Wyróżniono trzy jego zakresy: a/ dla formowania się struktury kolumnowej (strefa C): b/ dla transformacji struktury kolumnowej w strukturę w pełni równoosiową (okres inkubacji), C - E: Powstawanie struktury kolumnowej wyraźnie zwalania w okresie inkubacji. Wynika to z konkurencji między wzrostem struktury kolumnowej i równoosiowej. Postuluje się że zaobserwowana zależność dobrze odpowiada krytycznemu gradientowi temperatury, Gcrit.. Symulacja została przeprowadzona zarówno dla walców staliwnych jak i żeliwnych dla warunków zbliżonych do przemysłowych. Ponieważ tzw. inkubacja dzieli walec na dwie strefy (kolumnową i równoosiową) pewne eksperymenty związane z symulacją zostały przeprowadzone w skali półprzemysłowej celem konfrontacji z obliczeniami. Sformułowano równanie określające makrosegregację w obu strefach. Bazuje ono na ostatnio zaproponowanym równaniu dla opisu redystrybucji po dyfuzji wstecznej. Podkreślono rolę parametru dyfuzji wstecznej jako czynnika odpowiedzialnego za redystrybucję w obu strefach strukturalnych.
    Źródło:
    Archives of Metallurgy and Materials; 2012, 57, 1; 105-117
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies