Skocz do pozycji: 1.

Tytuł:: Effects Of Aluminum Sputtering On The Corrosion Resistance Of AZ91 Alloy
Wpływ glinu nanoszonego metodą rozpylania jonowego na odporność stopu AZ91 na korozję
Autorzy:: Ishibashi, Y.
Nose, M.
Hatakeyama, M.
Sunada, S.
Powiązania:: https://bibliotekanauki.pl/articles/355762.pdf
Data publikacji:: 2015
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: magnesium alloy
corrosion
aluminum
sputtering
stopy magnezu
korozja
glin
rozpylanie
Opis:: The corrosion resistance of a Magnesium alloy is low and needs to be improved. This research aimed at corrosion-resistance improvement by supatterd deposition aluminium film, which is formed on the surface of AZ91 Magnesium-alloy. Corrosion resistance performed polarization curve measurement, was evaluated in quest of the corrosion rate using the Tafel extrapolation method, and conducted surface observation and EDS analysis by SEM. Although corrosion resistance is not improved only by film forming because of defects in film, corrosion resistance is improved by heat treatment for 3 hours by 553K after sputtering. In the case of heat treated at 623K and 673K for 3 hours, magnesium diffuses through the alminium film and reached the surface of the film. Thus, heat treatment at high temperature degrade the corrosion resistance of the film. The optimization of heat treatment after sputtering is important in this method.
Celem badań jest zwiększenie odporności na korozję stopu magnezu AZ91 poprzez naniesienie na jego powierzchnię warstwy glinu metodą rozpylania jonowego. Na podstawie pomiarów krzywej polaryzacji, oszacowano szybkości korozji metodą ekstrapolacji Tafela. Obserwacje morfologiczne oraz badania składu chemicznego wykonano metodą SEM-EDS. Nie stwierdzono poprawy odporności na korozję stopu z powodu defektów obecnych w warstwie. Jak wykazały badania, obróbka cieplna napylonej warstwy w 553 K przez 3 godz. wpłynęła na poprawę odporności korozyjnej. Gdy obróbka cieplna prowadzona była w temperaturach 623 K i 673 K przez 3 godz., magnez dyfundował poprzez warstwę glinu aż do powierzchni warstwy. Z tego względu obróbka cieplna prowadzona w wysokiej temperaturze obniża odporność warstwy na korozję. Ważnym aspektem tej metody jest zatem optymalizacja procesu obróbki cieplnej warstwy po rozpylaniu.
Źródło:: Archives of Metallurgy and Materials; 2015, 60, 2A; 953-955
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Application of water-thinnable photopolymerizable resin for shaping of microreactors - preliminary results
Zastosowanie wodorozcieńczalnych, fotoutwardzalnych żywic do formowania mikroreaktorów - wstępne wyniki
Autorzy:: Falkowski, P.
Elert, P.
Powiązania:: https://bibliotekanauki.pl/articles/352994.pdf
Data publikacji:: 2011
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: wodorozcieńczalna żywica poliestrowa
glin
mikroreaktor
water-thinnable polyester resin
alumina
UV curing
microreactor
Opis:: The article presents the preliminary research on application of synthesized water-thinnable polyester resin for shaping of ceramic element by photopolymerization. The ceramic pastes made of alumina (30 vol%) and photocurable resins were used to prepare thin layers (tapes) and then were exposed to UV radiations. The cure depth and König hardness of cured layers were determined as well as the effect of a photoinitiator concentration on polymerization. The density of sintered ceramic samples also were examined. The research showed that the developed pastes with water-thinnable resin might be used to mold the ceramic elements by soft lithography method. The results obtained for polyester resin were compared with results obtained for commercially available photocurable resin.
W artykule przedstawiono wstępne wyniki badań dotyczące zastosowania zsyntezowanej wodorozcieńczalnej żywicy poliestrowej w metodzie formowania elementów ceramicznych z zastosowaniem procesu fotopolimeryzacji. Z otrzymanych z tlenku glinu (30%obj) i ulegającej polimeryzacji żywicy poliestrowej past ceramicznych formowano cienkie warstwy, które następnie poddawano działaniu promieniowania UV powodującemu sieciowanie się żywicy. Następnie badano twardość Koniga otrzymanych warstw, wpływ ilości fotoinicjatora oraz głębokość na jaką zachodził proces fotopolimeryzacji. Wyznaczono także gęstość otrzymanych spieków. Przeprowadzone badania wykazały, że otrzymane pasty z wodorozcieńczalnej żywicy poliestrowej mogą być wykorzystane w formowaniu elementów ceramicznych metodą litografii miękkiej. Wyniki otrzymane dla past z żywicą poliestrową zostały porównane do wyników otrzymanych z handlowo dostępną swiatłoutwardzalną żywicą.
Źródło:: Archives of Metallurgy and Materials; 2011, 56, 4; 1177-1183
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 3.

Tytuł:: Galactose monoacrylate as a new monomer in gelcasting process
Monoakrylan galaktozy jako nowy monomer w procesie odlewania żelowego
Autorzy:: Szudarska, A.
Mizerski, T.
Szafran, M.
Powiązania:: https://bibliotekanauki.pl/articles/352986.pdf
Data publikacji:: 2011
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: odlewanie żelowe
glin
monosacharydy
monomery nietoksyczne
gelcasting
alumina
monosaccharides
deflocculants
low-toxic monomers
Opis:: The present work shows the results of following the recently developed trend to design new low toxic monomers which can be applied in gelcasting process. New compound, 6-O-acryloyl-D-galactose (galactose monoacrylate) has been synthesised and its effectiveness as processing agent has been studied. The results are compared with those reported so far regarding applying some other new monomers - 3-O-acryloyl-D-glucose and glycerol monoacrylate in gelcasting technology. The influence of spatial structure of obtained monomers on rheological properties of alumina suspensions and properties of green bodies is discussed as well.
Artykuł przedstawia wyniki badań dotyczących zastosowania nowozsyntezowanej akrylowej pochodnej galaktozy jako monomeru w procesie odlewania żelowego. Opracowano metode syntezy 6-O-akryloilogalaktozy oraz zbadano jej role i efektywność w procesie. Wyniki porównano z wcześniejszymi pracami z tego zakresu, dotyczącymi zastosowania innych nowych nietoskycznych monomerów – 3-O-akryloiloglukozy oraz monoakrylanu glicerolu, szukając wpływu budowy przestrzennej cząsteczek monomeru na właściwości reologiczne mas lejnych z tlenku glinu i właściwosci odlanych z nich wyrobów.
Źródło:: Archives of Metallurgy and Materials; 2011, 56, 4; 1211-1215
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 4.

Tytuł:: Properties of water-based slurries for fabrication of ceramic-metal composites by slip casting method
Własciwości wodnych zawiesin do otrzymywania kompozytów ceramika-metal metodą odlewania mas lejnych
Autorzy:: Gizowska, M.
Konopka, K.
Szafran, M.
Powiązania:: https://bibliotekanauki.pl/articles/352894.pdf
Data publikacji:: 2011
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: glin
kompozyty metalowo-ceramiczne
nikiel
odlewanie z mas lejnych
potencjał zeta
alumina
ceramic-metals composites
nickel
slip casting
zeta potential
Opis:: The main advantage of ceramic-metal composites is the increase of fracture toughness of the brittle ceramic matrix. The slip casting method gives the possibility to obtain products of complicated shapes without green machining.In the work results concerning colloidal and rheological aspects of ceramic-metal composite fabrication via the slip casting method are presented. Slurry consisted of ceramic (?-Al2O3) and nickel powder suspended in water with addition of deflocculants composition (citric acid and diammonium citrate), surface-active agents and binder. Ceramic and metallic powders show great differences in electrokinetic behavior, which cause that the heteroflocculation effect in the suspension can take place. In order to investigate the particles interaction characteristics, the zeta potential of each powder was examined. The zeta potential measurements were performed for diluted suspensions as a function of pH. Rheological measurements of the slurries were performed. Although surface of alumina was modified, so that the electrokinetic behavior resembled one of nickel, it turned out that the presence of nickel particles has great influence on the slurry properties. The change of rheological properties for slurries containing nickel particles results probably from strong interaction between alumina and nickel particles.
Do korzystnych cech ceramiki można zaliczyć dużą twardość, sztywność, odporność na ścieranie oraz niską gęstość. Jednak kruchość tych materiałów ogranicza obszar ich zastosowania. Jedna z metod zwiększenia odporności na kruche pękanie jest realizowane poprzez wprowadzenie plastycznych cząstek metalu do osnowy ceramicznej. Przedstawiono wyniki badań właściwości mas lejnych do otrzymywania kompozytów o osnowie z tlenku glinu z rozproszonymi cząstkami niklu metodą odlewania z mas lejnych na bazie proszków metalicznego i ceramicznego. W skład mas lejnych wchodziła mieszanina proszku tlenku glinu i niklu oraz układ upłynniaczy, środek powierzchniowoczynny i spoiwo. Materiały wykorzystane w badaniach charakteryzują się dużą różnicą ich właściwości elektrokinetycznych, przez co w ich mieszaninie może dochodzić do efektu heteroflokulacji (przyciągania się elektrostatycznego cząstek o różnego rodzaju i o róznym ładunku). W niniejszej pracy przedstawiono opis zjawisk elektrokinetycznych występujących w układzie tlenek glinu i nikiel na podstawie pomiarów potencjału zeta zarówno w wodzie, jak i w roztworze upłynniaczy stosowanych w masie lejnej. Ponadto przeprowadzono badania własciwości reologicznych w celu określenia wpływu obecności cząstek metalicznych w masie lejnej na właściwości zawiesiny. Wprowadzane do masy lejnej środki upłynniające modyfikują powierzchnie tlenku glinu minimalizując aglomeracje cząstek związaną z efektem heteroflokulacji. Pomimo to zaobserwowano znaczny wpływ obecności cząstek niklu na właściwości reologiczne mas lejnych.
Źródło:: Archives of Metallurgy and Materials; 2011, 56, 4; 1105-1110
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "Glin" wg kryterium: Temat

Źródło danych