Silver Matrix Composite Reinforced by Aluminium-Silver Intermetallic Phases
Autorzy:
Wloch, G.
Skrzekut, T.
Sobota, J.
Woznicki, A.
Błaż, L.
Powiązania:
https://bibliotekanauki.pl/articles/352667.pdf
Data publikacji:
2017
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
silver-aluminum composite
plastic consolidation
powder metallurgy
Ag-Al intermetallics
Opis:
Silver and aluminum powders (82 mass % Ag and 18 mass % Al) were mixed and hot extruded at 673 K with extrusion ratio λ = 25. Performed X-ray diffraction analysis of as extruded rod revealed the development of Ag3Al and Ag2Al-type intermetallic phases. Structural observations and both chemical and diffraction analysis of structural components confirmed the growth of mentioned phases in the vicinity of elementary Al and Ag granules. No pores or voids were observed in the material. Mechanical properties of the composite, UTS = 490MPa, YS = 440 MPa, HV2 = 136, were relatively high if compared to commercial Ag and Cu products. Hot compression tests pointed to the good hot workability of the composite at deformation temperature range 473 K - 773 K. The differential scanning calorimetry tests were performed in order to estimate structural processes during heating of Ag/Al composite that lead to thermodynamically stable liquid state. It was found that characteristic temperature of three endothermic peaks correspond to (1) peritectoid transformation μ-Ag3Al → ζ-Ag2Al + (Ag), (2) the eutectic melting ζ-Ag2Al + (Al) → L, (3) melting of the ζ-Ag2Al phase. The Vickers hardness of the samples annealed at 673 K, for the time range up to 6900 minutes, was also determined. It was concluded that mutual diffusion of elements between Ag and Al granules and the growth of μ-Ag3Al and ζ-Ag2Al grains during annealing at 673 K result in a slight hardening of the composite.
Źródło:
Archives of Metallurgy and Materials; 2017, 62, 1; 427-434
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies