- Tytuł:
- Physical properties study of the CeOsGa₄ compound
- Autorzy:
-
Sondezi, B.
Strydom, A. - Powiązania:
- https://bibliotekanauki.pl/articles/1047645.pdf
- Data publikacji:
- 2018-03
- Wydawca:
- Polska Akademia Nauk. Instytut Fizyki PAN
- Tematy:
-
75.50.Ee
75.50.Cc
75.40.-s - Opis:
- A polycrystalline sample of CeOsGa₄ was prepared by arc-melting stoichiometric quantities of high purity elements of 4N and greater, in an arc furnace. The data was confirmed to crystallize in an orthorhombic structure, with a space group Pmma (Number 51). Measurements of the magnetic susceptibility showed a distinct anomaly around T_{o} = 3.8 K, while the high temperature data (above 100 K) obeys Curie-Weiss law. The calculated effective moment of 2.44 μ_{B}, was obtained, which was a bit less than the theoretical moment for a Ce³⁺ ion of 2.54 μ_{B}. Magnetization data at T=2 K depicts that CeOsGa₄ does not saturate up to applied magnetic field of 7 T, while the data measured at 9 K indicates that the compound is purely paramagnetic at that temperature. The low temperature specific heat data is characterized by an anomaly at T_{o} = 3.8 K confirming the χ(T) data. Electrical resistivity shows a metallic behaviour at high temperatures with a deviation at low temperatures, signalling the cooperative behaviour which results to ordering. In this work we present the initial studies of the physical properties measurements performed on this compound.
- Źródło:
-
Acta Physica Polonica A; 2018, 133, 3; 398-400
0587-4246
1898-794X - Pojawia się w:
- Acta Physica Polonica A
- Dostawca treści:
- Biblioteka Nauki