- Tytuł:
- Effect of Post Annealing on La$\text{}_{0.7}$Sr$\text{}_{0.3}$MnO$\text{}_{3}$ Thin Films
- Autorzy:
-
Cheng, W. F.
Leung, C. W. - Powiązania:
- https://bibliotekanauki.pl/articles/2047232.pdf
- Data publikacji:
- 2007-01
- Wydawca:
- Polska Akademia Nauk. Instytut Fizyki PAN
- Tematy:
-
75.30.-m
73.50.-h - Opis:
- The stability of La$\text{}_{0.7}$Sr$\text{}_{0.3}$MnO$\text{}_{3}$ thin films fabricated by pulsed laser deposition, under different annealing procedures, was investigated. La$\text{}_{0.7}$Sr$\text{}_{0.3}$MnO$\text{}_{3}$ films were deposited on (100) LaAlO$\text{}_{3}$ substrates at 650ºC with the films thickness from 20 to 50 nm. The oxygen pressures used to fabricate the films were 150 mTorr and 100 mTorr. Then in situ annealing steps were performed at 100 and 150 mTorr, respectively. Curie temperatures (T$\text{}_{c}$) of the films were estimated from the peaks of the temperature dependent resistance data. For the films deposited at 100 mTorr and annealed at 150 mTorr, T$\text{}_{c}$ slightly dropped for short annealing time and recovered to 360 K for 30 min annealing. For the films deposited at 100 mTorr and annealed at 150 mTorr, it maintained semiconducting behavior without transition after annealing up to 30 minutes. For ex situ post annealing, it was found that the T$\text{}_{c}$ of the films strongly depended on the annealing procedures.
- Źródło:
-
Acta Physica Polonica A; 2007, 111, 1; 117-122
0587-4246
1898-794X - Pojawia się w:
- Acta Physica Polonica A
- Dostawca treści:
- Biblioteka Nauki
Artykuł