Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "sodium silicate sands" wg kryterium: Temat

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-9 z 9
    Tytuł:
    Study on Reclamation of CO2-hardened Sodium Silicate Used Sands by CaO Powder
    Autorzy:
    Lu, Jijun
    Yang, Lei
    Qian, Jiangbing
    He, Wei
    Wang, Huafang
    Powiązania:
    https://bibliotekanauki.pl/articles/2174624.pdf
    Data publikacji:
    2022
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    sodium silicate sands
    reclamation
    orthogonal experiment
    wet reclamation
    dry reclamation
    hardening of the sands
    masa krzemianowo-sodowe
    regeneracja
    utwardzanie
    eksperyment
    Opis:
    Aiming at the problems of wet reclamation consuming a lot of water, dry (mechanical) reclamation having wear and power consumption, this paper to find suitable reclamation reagents to reduce the influence of harmful substances in used sodium silicate sands. By comparing the reclamation effect of CaO, Ca(OH)2 and Ba(OH)2 reclamation powder reagents, it was concluded that CaO had the best reclamation effect. Through the single factor experiment, the influence of CaO on the reclamation effect was explored: 1. addition amount of CaO; 2. the additional amount of water; 3. reclamation time. The orthogonal results showed that the CaO reclamation effect was the best when the amount of CaO was 1.5%, the amount of sodium silicate was 4.0%, the amount of water added was 6.0%, and the reclamation time was 12.0h. In this experiment, 82.2% carbonate and 75.0 % silicate in used sands can be removed. The microscopic analysis of the reclamation sands was carried out by scanning electron microscope (SEM); The surface was relatively smooth, without large area cracks and powder accumulation. Compared with the used sands, the instant, 24h ultimate, and residual strengths of the reclaimed sands were increased by 536.5%, 458.1%, and 89.8%, respectively, which was beneficial to the reclamation of the CO2 sodium silicate used sands.
    Źródło:
    Archives of Foundry Engineering; 2022, 22, 3; 99--106
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Effect of Methyl Silicone Oil to Moisture Resistance of Sodium Silicate Sands by Microwave Hardening
    Autorzy:
    Wang, Huafang
    Gao, Xiang
    Yang, Lei
    He, Wei
    Lu, Jijun
    Powiązania:
    https://bibliotekanauki.pl/articles/2126894.pdf
    Data publikacji:
    2022
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    sodium silicate sands
    microwave hardening
    methyl silicon oils
    moisture absorption
    piaski sodowo-krzemianowe
    hartowanie mikrofalowe
    olej metylosilikonowy
    wchłanianie wilgoci
    Opis:
    The sodium silicate sands hardened by microwave have the advantages of high strength, fast hardening speed and low residual strength with the lower addition of sodium silicate. However, the sodium ion in the sands will absorb moisture from the atmosphere, which would lead to lower storing strength, so the protection of a bonding bridge of sodium silicate between the sands is crucial. Methyl silicone oil is a cheap hydrophobic industrial raw material. The influence of the addition amount of methyl silicone oil modifier on compressive strength and moisture absorption of sodium silicate sands was studied in this work. The microscopic analysis of modified before and after sodium silicate sands has been carried on employing scanning electron microscopy(SEM) and energy spectrum analysis(EDS). The results showed that the strength of modified sodium silicate sands was significantly higher than that of unmodified sodium silicate sands, and the best addition of methyl silicone oil in the quantity of sodium silicate was 15%. It was also found that the bonding bridge of modified sodium silicate sands was the density and the adhesive film was smooth, and the methyl silicone oil was completely covered on the surface of the sodium silicate bonding bridge to protect it.
    Źródło:
    Archives of Foundry Engineering; 2022, 22, 1; 43--47
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Impact of Density Degree and Grade of Inorganic Binder on Behavior of Molding Sand at High Temperature
    Autorzy:
    Stachowicz, M.
    Paduchowicz, P.
    Granat, K.
    Powiązania:
    https://bibliotekanauki.pl/articles/106947.pdf
    Data publikacji:
    2017
    Wydawca:
    Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Wydawnictwo AGH
    Tematy:
    foundry
    hydrated sodium silicate
    hot-distortion
    thermal deformation
    molding sands
    Opis:
    This paper discusses the impact of high temperatures (up to 900°C) on molding and core sand with inorganic binders selected from among the group of unmodified grades of hydrated sodium silicate (water-glass). Molding sands with medium quartz sand were made under laboratory conditions and compacted at the different energy inputs necessary for obtaining various apparent densities (ϱ0). Due to the different composition and apparent density of molding mixtures hardened via microwaves at a frequency of 2.45 GHz, it was possible to assess their deformation (L) at a high temperature above the binder’s eutectic temperature. For this purpose, an apparatus for hot distortion tests was used whose construction and equipment allows us to measure the thermoplastic deformations in molding sand in many aspects; i.e., in its time of annealing. The article proposes new possibilities of interpreting the hot distortion phenomena in comparative studies of molding materials and mixtures. The application of this new measurement method revealed the differences between molding mixtures made with five inorganic binders with a molar module ranging from 2.0 to 3.4 and apparent density ranging from 1.34 to 1.57 g/cm3. It was established that distortions under the influence of high temperatures last the longest in molding sand with a binder with the highest molar module (3.4). Research also revealed that the density of molding sand is significant for increasing/decreasing the rate of thermoplastic deformations following the heating of samples only if the molding sand includes binders with a molar module of between 3.0 to 3.4. For molding sand with binders with molar modules from 2.0 to 2.5, it was established that this is excessively susceptible to thermoplastic deformation.
    Źródło:
    Journal of Casting & Materials Engineering; 2017, 1, 3; 64-69
    2543-9901
    Pojawia się w:
    Journal of Casting & Materials Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Selection of Hardening Technology of Moulding Sand with Hydrated Sodium Silicate Binder Devoted to Aluminum Alloys Ablation Casting
    Autorzy:
    Major-Gabryś, K.
    Hosadyna-Kondracka, M.
    Grabarczyk, A.
    Kamińska, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/354196.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    foundry engineering
    ablation casting
    moulding sands
    hydrated sodium silicate
    hot-box technology
    Opis:
    The ablation casting technology consists in pouring castings in single-use moulds made from the mixture of sand and watersoluble binder. After pouring the mould with liquid metal, while the casting is still solidifying, the mould destruction (washing out, erosion) takes place using a stream of cooling medium, which in this case is water. The following paper focuses on the selection of moulding sands with hydrated sodium silicate technologies for moulds devoted to the ablation casting of aluminum alloys. It has been proposed to use different types of moulding sands with a water-soluble binder, which is hydrated sodium silicate. The authors showed that the best kind of moulding sands for moulds for Al alloy casting will be moulding sands hardened with physical factors – through dehydration. The use of microwave hardened moulding sands and moulding sands made in hot-box technology has been proposed. The tests were carried out on moulding sands with different types of modified binder and various inorganic additives. The paper compares viscosity of different binders used in the research and thermal degradation of moulding sands with tested binders. The paper analyzes the influence of hardening time periods on bending strength of moulding sands with hydrated sodium silicate prepared in hot-box technology. The analysis of literature data and own research have shown that molding sand with hydrated sodium silicate hardened by dehydration is characterized by sufficient strength properties for the ablation foundry of Al alloys.
    Źródło:
    Archives of Metallurgy and Materials; 2019, 64, 1; 359-364
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Reclaiming Ability of Spent Sands with Modified, Hydrated Sodium Silicate
    Autorzy:
    Kamińska, J.
    Kmita, A.
    Powiązania:
    https://bibliotekanauki.pl/articles/380608.pdf
    Data publikacji:
    2014
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    moulding sands
    hardening
    Floster S process
    modification of sodium silicate
    reclamation
    masa formierska
    utwardzanie
    modyfikacja krzemianu sodowego
    regeneracja
    Opis:
    The presented in the paper investigations were aimed at the determination of the reclaimed material (obtained in the dry mechanical reclamation process) addition influence on properties of moulding sands with hydrated sodium silicate modified by colloidal suspension of zinc oxide nanoparticles in propanol. Nanoparticles originated from the thermal decomposition of alkaline zinc carbonate, were used. The results of the reclamation of the spent moulding sand with hydrated sodium silicate performed in the AT-2 testing reclaimer are presented in the paper. Both, spent sands from the Floster S technology and from the technology with the modified water-glass were subjected to the reclamation processes. The following determinations of the reclaimed material were performed: pH reaction, acid demand, ignition loss and Na2O content. The obtained reclaim was used as a matrix component of moulding sands with water-glass in the Floster S technology, in which it constituted 60% and 50% of the sand matrix. The strength properties of the prepared moulding sands were determined (bending strength Rgu, tensile strength Rmu) after samples storing times: 1h, 2h, 4h and 24 hours.
    Źródło:
    Archives of Foundry Engineering; 2014, 14, 1; 41-44
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Microwave-Hardened Moulding Sands with Hydrated Sodium Silicate for Modified Ablation Casting
    Autorzy:
    Puzio, S.
    Kamińska, J.
    Major-Gabryś, K.
    Angrecki, M.
    Hosadyna-Kondracka, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/379775.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    ablation casting
    moulding sands
    environmental protection
    hydrated sodium silicate
    microwave hardening
    odlewanie
    masy formierskie
    ochrona środowiska
    krzemian sodu
    hartowanie mikrofalowe
    Opis:
    The aim of this study is to demonstrate the possibility of using moulds made from the environmentally friendly sands with hydrated sodium silicate in modified ablation casting. The ablation casting technology is primarily intended for castings with diversified wall thickness and complex shapes made in sand moulds. The article presents the effect of binder content and hardening time on the bending strength Rgu of moulding sands with binders based on hydrated sodium silicate hardened by microwave technology. The aim of the research was to develop an optimal sand composition that would provide the strength necessary to make a mould capable of withstanding the modified ablation casting process. At the same time, the sand composition should guarantee the susceptibility of the mould to the destructive action of the ablation medium, which in this case is water. Tests have shown that microwave hardening provides satisfactory moulds’ strength properties even at a low binder content in the sand mixture.
    Źródło:
    Archives of Foundry Engineering; 2019, 2; 91-96
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Kompozycje: uwodniony krzemian sodu – materiał biodegradowalny, jako spoiwo mas formierskich
    Compositions: Hydrated Sodium Silicate – Biodegradable Material, as Moulding Sands Binder
    Autorzy:
    Grabarczyk, A.
    Major-Gabryś, K.
    Dobosz, S. M.
    Wojczuk, M.
    Superson, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/380754.pdf
    Data publikacji:
    2014
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    masy formierskie
    spoiwo
    uwodniony krzemian sodu
    materiał biodegradowalny
    Polikaprolakton
    PCL
    utwardzacz estrowy
    moulding sands
    binder
    hydrated sodium silicate
    biodegradable material
    polycaprolactone
    Opis:
    Zaostrzające się wymogi dotyczące ochrony środowiska wywierają nacisk na poszukiwanie nowych proekologicznych rozwiązań w wielu dziedzinach przemysłu. Przepisy te dotyczą także technologii wytwarzania mas formierskich. W niniejszej publikacji autorzy podjęli próbę zastosowania kompozycji: uwodniony krzemian sodu – materiał biodegradowalny, jako spoiwo mas formierskich. Badany dodatek biodegradowalny jest substancją organiczną, ale przyjazną dla środowiska. Ocena wpływu materiału biodegradowalnego na parametry masy formierskiej została dokonana w oparciu o badania wybranych właściwości technologicznych: wytrzymałości na zginanie Rgu i ścieralności S oraz o badania wybijalności mas ocenianej przez pomiar wytrzymałości końcowej na ściskanie Rctki ekspansji wysokotemperaturowej ΔV. Badaniom poddano masy z uwodnionym krzemianem sodu sporządzane w technologii estrowej utwardzane utwardzaczami opartymi o estry kwasu węglowego- Jeffsol BC, Ixional SD. Utwardzacze te zostały opracowane w Pracowni Tworzyw Formierskich Wydziału Odlewnictwa AGH w celu poprawy jakości regeneratu mas z uwodnionym krzemianem sodu. Autorzy zaproponowali zastosowanie jako składnika wyżej wymienionej kompozycji, biodegradowalnego polikaprolaktonu (PCL). Przeprowadzone badania wykazały, że dodatek 5% PCL nie pływa negatywnie na właściwości technologiczne badanych mas, zatem jego stosowanie jest celowe i uzasadnione.
    Environmental protection regulations are becoming more and more strict which puts pressure on finding new proecological solutions in many industries. These regulations concern also the technology of moulding sands preparation. In this work the authors made an attempt to apply composition: hydrated sodium silicate - biodegradable material, as the moulding sand binder. The examined biodegradable additive is an organic substance, but it is environment-friendly. Assessment of the biodegradable material’s impact on the moulding sand’s parameters was made based on the chosen technological parameters: bending strength Rgu and wearability S, knock-out properties of the moulding sands were measured based on final compressive strength Rctk and thermal expansion ΔV. The tests were carried on moulding sands with hydrated sodium silicate in ester technology with hardeners based on carbonite esters: Flodur 3, Jeffsol BC, Ixional SD. The hardeners were developed in Moulding Sands Workshop on Faculty of Foundry Engineering AGH to improve the quality of reclaimed moulding sands with hydrated sodium silicate. Authors proposed using biodegradable polycaprolactone (PCL) as an element of the above-mentioned composition. The conducted research showed that biodegradable additive – PCL (polycaprolactone), does not have a negative influence on technological properties of the tested moulding sands, thus its’ usage is intentional and justified.
    Źródło:
    Archives of Foundry Engineering; 2014, 14, 4 spec.; 37-42
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Badania wstępne utwardzanych mikrofalowo połączeń wykonanych z klejów sporządzonych na bazie uwodnionego krzemianu sodu i piasku kwarcowego
    Preliminary testing of microwave-cured joints made of adhesives based on hydrated sodium silicate and quartz sand
    Autorzy:
    Stachowicz, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/391741.pdf
    Data publikacji:
    2018
    Wydawca:
    Sieć Badawcza Łukasiewicz - Instytut Odlewnictwa
    Tematy:
    odlewnictwo
    masa formierska i rdzeniowa
    rdzenie odlewnicze
    uwodniony krzemian sodu
    klej
    casting
    moulding and core sands
    casting cores
    hydrated sodium silicate
    adhesive
    Opis:
    W pracy podjęto próbę wyjaśnienia zjawisk towarzyszących powstawaniu i niszczeniu połączeń klejonych elementów form i rdzeni, w których jako kleje zastosowano mieszaninę niemodyfikowanego uwodnionego krzemianu sodu o module molowym 2,9 (SiO2/Na2O) i nośnika, którym był bardzo drobny piasek kwarcowy. Mieszaniny sporządzanych klejów wykonano według własnych propozycji składu i opisów patentowych. Na podstawie dostępnych danych literaturowych opracowano metodykę wytwarzania i badania wytrzymałości na rozciąganie połączeń klejonych z użyciem dzielonych kształtek ósemkowych typu dog-bone. Przeznaczone do klejenia połówki kształtek ósemkowych typu dog-bone wykonano z utwardzonej mikrofalowo kwarcowej masy z uwodnionym krzemianem sodu o module molowym 2,5 (SiO2/Na2O). Do utwardzenia klejonych połączeń również zastosowano metodę nagrzewania falą elektromagnetyczną o częstotliwości 2,45 GHz. Wyniki badań zrywania sklejonych połówek kształtek typu dog-bone, w ich najmniejszym przekroju, odniesiono do prób wytrzymałości standardowych kształtek ósemkowych oraz do połączeń klejonych znanych z opisów patentowych. Wyniki badań obciążeń krytycznych połączeń klejonych uzupełniono obserwacjami SEM po próbach rozciągania. Na podstawie przeprowadzonych badań ustalono, że wytrzymałość takich połączeń przewyższa wytrzymałość masy formierskiej, a destrukcja sklejonych kształtek ósemkowych odbywa się w strefach przy powierzchniach, na które naniesiono sporządzone nieorganiczne kleje.
    In this paper an attempt was made to explain the phenomena accompanying the formation and destruction of bonded elements of moulds and cores in which a mixture of unmodified hydrated sodium silicate with a molar module of 2.9 (SiO2/Na2O) and a carrier – very fine quartz sand – was used as adhesives. Mixtures of prepared adhesives were made according to own compositional proposals and patent descriptions. On the basis of available literature data, the methodology of production and tensile strength testing of bonded joints with the use of divided octagonal dog-bone shapes was worked out. Dog-bone shaped pieces intended for binding were made of microwave-cured quartz sand with hydrated sodium silicate of molar module 2.5 (SiO2/Na2O). For the curing of bonded joints the electromagnetic wave heating method of 2.45 GHz was also applied. The results of tearing off the bonded halves of dog-bone shaped pieces in their smallest cross-section were related to the tensile strength tests of standard octagonal shaped pieces and to bonded joints known from patent descriptions. The results of critical loads of bonded joints were supplemented with SEM observations after tensile tests. On the basis of the conducted tests it was found that the tensile strength of such joints exceeds the tensile strength of the moulding sand, and the destruction of the bonded octagonal shapes takes place in areas near the surfaces on which inorganic adhesives were applied.
    Źródło:
    Prace Instytutu Odlewnictwa; 2018, 58, 4; 295-308
    1899-2439
    Pojawia się w:
    Prace Instytutu Odlewnictwa
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Analiza metod pomiaru wybijalności mas formierskich
    The Analysis of Moulding Sands’ Knock-Out Properties Measurement Methods
    Autorzy:
    Major-Gabryś, K.
    Grabarczyk, A.
    Kaźnica, N.
    Powiązania:
    https://bibliotekanauki.pl/articles/380862.pdf
    Data publikacji:
    2014
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    masa formierska
    wybijalność
    ekspansja wysokotemperaturowa
    wytrzymałość na ściskanie
    uwodniony krzemian sodu
    molding sands
    knock-out properties
    high-temperature expansion
    compressive strength
    hydrated sodium silicate
    Opis:
    Potrzeba uzyskiwania wysokiej jakości odlewów wymusza podejmowanie prac badawczych dla otrzymania mas formierskich i rdzeniowych zapewniających uzyskanie tworzyw o odpowiednich parametrach technologicznych, jednocześnie spełniających wysokie wymogi ochrony środowiska. Przyjaznymi dla środowiska są masy ze spoiwami nieorganicznymi, jednak jedną z ich podstawowych wad jest zła wybijalność. W artykule zostały przedstawione najczęściej stosowane metody pomiaru wybijalności mas formierskich i rdzeniowych. Autorzy zaproponowali nową metodę oceny wybijalności opierającą się na pomiarze ekspansji wysokotemperaturowej. Przedstawiono ocenę wybijalności mas z uwodnionym krzemianem sodu modyfikowanym dodatkiem nanocząstek Al2O3 w oparciu o ekspansje wysokotemperaturową oraz pomiar wytrzymałości końcowej na ściskanie Rctk. Autorzy udowodnili, że ekspansja wysokotemperaturowa stanowić może kryterium oceny wybijalności mas formierskich.
    The necessity of receiving high quality castings forces undertaking research to elaborate moulding and core sands ensuring obtaining the materials with relevant technological parameters and also with high environmental standards. Environmental friendly are moulding sands with inorganic binders. Unfortunately, their fundamental disadvantages are weak knock-out properties. The article presents the most commonly used methods of measuring the knock-out properties of moulding and core sands. The authors propose a new method for estimation this parameter of moulding sands with hydrated sodium silicate modified with nanoparticles of Al2O3. The method is based on the measurement of high-temperature expansion. There are shown moulding sands’ knock-out properties estimated according to high-temperature expansion measurement and according to retained strength Rc tk measurement. Authors proved that high-temperature expansion may be the standard of moulding sands’ knock-out properties estimation.
    Źródło:
    Archives of Foundry Engineering; 2014, 14, 3 spec.; 35-40
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-9 z 9

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies