In this paper the electrodeposition of boron on the surface of cast iron as a coating is applied to increase the hardness and
protect the substrate against abrasive wear. The boron containing coating was synthesized by electrodeposition process from
a NaCl-KCl (1:1 mol)-10 w%NaF-10w% KBF4 molten salt. The effect of electrolysis parameters (temperature and time) on the
hardness is presented; the current density varied in the range –37 – –4.5 mA/cm2, allowing perfect coverage of and respect for
dimensions. The electrochemical process was carried out at different temperatures (750°C-900°C) and for different periods of time
(5-10 hours). Depending on the current density and duration of electrolysis, the deposits consist of FeB or Fe2B. Microhardness
measurements across the boride layer indicated very high hardness values (between 1600 and 2100 HV0.05).The structure of the
boride layer is linked to its boron content and thermal history: as-deposited coatings present very small grain sizes and can be
considered as nearly amorphous.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00