Viscosity and creep compliance of polyoxymethylene copolymers of various average molecular weights

The effect of average molecular weight (M_w ) of polyoxymethylene (POM) on melt viscosity and solid state creep compliance were investigated. Viscosity follows the power function of M_w. Creep compliance results indicate that time-temperature superposition applies to POM copolymers. Creep compliance in ashort time (0.25 s) is independent of M_w, but in a longer time (10 years) it follows an inverse power law relation with M_w, up to a critical value of M_w = 81 100, where creep compliance becomes independent of M_w. At intermediate time (17 min), similar to short one, no effect on susceptibility to creep compliance was observed. It was also stated that the activation energy is independent of M_w.

Zbadano wpływ średniego ciężaru cząsteczkowego (M_w) wybranych kopolimerów polioksymetylenowych (POM) na lepkość stopu i podatność na pełzanie próbki w stanie stałym. Stwierdzono, że w przypadku wszystkich badanych kopolimerów POM zależność lepkości od M_w opisuje funkcja potęgowa. Wyniki badań podatności na pełzanie wykazały zgodność z zasadą równoważności temperaturowo-czasowej. Podatność na pełzanie w krótkim czasie (0,25 s) była niezależna od M_w, natomiast w czasie dłuższym (10 lat) wielkość ta zmniejszała się ze zwiększaniem M_w, aż do wartości krytycznej M_c = 81 100, po której nie zależała już od M_w. W średnim czasie (17 min), podobnie jak w czasie krótkim, M_w nie wpływał na podatność na pełzanie. Zaobserwowano również, że energia aktywacji nie jest funkcją M_w.