Analysis of the decay of some effects of modification of polylactide surface layers

The results of an investigation into the effects of modifying a surface layer (SL) of polylactide (PLA) as a function of time are presented. The PLA modification was performed by the method of corona discharges (CD) in the air using unit energy values (E_u) equal to 3.5 and 10 kJ/m². The extent of oxidation and contact angle of the SL were determined by the methods of X-ray photoelectron spectroscopy (XPS) and goniometry, respectively. The measurements were carried out immediately after the modification process, as well as 1, 2, and 3 months later.

Analizowano zanik wczasie zmian wywołanych modyfikowaniem za pomocą wyładowań koronowych (CD) warstwy wierzchniej (SL) polilaktydu (PLA). Modyfikowanie prowadzono w atmosferze powietrza, z zastosowaniem jednostkowej energii (E_u) modyfikowania o wartości 3,5 i 10 kJ/m². Stopień utlenienia oraz wartość kąta zwilżania SL badano metodą spektroskopii fotoelektronowej (XPS) oraz goniometrii, bezpośrednio po procesie modyfikowania oraz po upływie 1, 2 i 3 miesięcy.