Production and characterization of poly(urea-urethane) elastomers synthetized from rapeseed oil-based polyols. Part I. Structure and properties

Poly(urea-urethane)s (PUUR), wherein the polyol substrates of petrochemical origin, partly replaced by vegetable polyols, were synthesized. Various contents of polyols derived from rapeseed oil – from 0 to 50wt% were used. In order to determine the chemical structure of the obtained samples, they were examined using Fourier transform infrared spectroscopy (FT-IR). Physicochemical and mechanical properties were determined using, among others, methods of differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA), as well as the tribological tests were performed. Studies have shown that new material obtained using the highest content of the polyol of vegetable origin (50 wt%) was characterized by the best storage modulus and friction coefficient. This material can be applied where low abrasive wear and volume resistivity is required.

W ramach pracy zsyntetyzowano poliuretanomoczniki (PUUR), w których substraty poliolowe pochodzenia petrochemicznego zastępowano częściowo poliolami pochodzenia roślinnego. Zastosowano różne zawartości polioli pochodzących z oleju rzepakowego – od 0 do 50% mas. substratów poliolowych. Metodą spektroskopii w podczerwieni z transformacją Fouriera (FT-IR) określono strukturę chemiczną otrzymanych próbek PUUR. Właściwości fizykochemiczne i mechaniczne określano, odpowiednio, metodą różnicowej kalorymetrii skaningowej (DSC) i dynamicznej analizy mechanicznej (DMA). Przeprowadzono również testy trybologiczne. Badania wykazały, że najlepszą wartością składowej rzeczywistej modułu zespolonego (E') iwspółczynnika tarcia charakteryzował się materiał zawierający 50% mas. poliolu pochodzenia roślinnego. Materiał ten może znaleźć zastosowanie w wyrobach, dla których wymagane jest małe zużycie ścierne i mała rezystywność skrośna.