Ternary potato starch-furcellaran-gelatin film – a new generation of biodegradable foils

Foils were prepared from potato starch (S), furcellaran (F) and gelatin (G) (S/F/G foils) using glycerol as a plasticizer. Their mechanical properties, aqueous solubility, water content, water uptake, enzymatic hydrolysis, and thermal (DSC) properties were determined. The 0.16 mm thick foil has ~ 80 MPa mechanical resistance with an elongation at break of 27.8 %. The aqueous solubility and water uptake of the S/F/G foils reached 35 % and 145 %, respectively. The S/F/G foils were susceptible to hydrolysis with polysaccharide enzymes such as glucoamylase and Viscozyme L (a blend of arabanase, cellulase, β-glucanase, hemicellulase and xylanase), as well as trypsin, a proteinase.

Z mieszaniny skrobi ziemniaczanej (S), furcellaranu (F) i żelatyny (G) oraz glicerolu jako plastyfikatora otrzymywano trójskładnikową folię S/F/G. Zbadano właściwości mechaniczne, rozpuszczalność, zawartość wody, wodochłonność, podatność na hydrolizę enzymatyczną oraz właściwości termiczne (DSC) wytworzonej folii. Folia o grubości ok. 0,16 mm wykazywała wytrzymałość mechaniczną ~ 80 MPa, a jej wydłużenie przy zerwaniu wynosiło 27,8 %. Folia S/F/G charakteryzowała się małą rozpuszczalnością (ok. 35 %) i wodochłonnością (ok. 145 %). Zbadano kinetykę reakcji hydrolizy enzymatycznej folii S/F/G w obecności enzymów polisacharydowych: glukoamylazy i Viscozyme L (mieszanina enzymów arabinazy, celulazy, β-glukanazy, hemicelulazy, ksylanazy) oraz enzymu białkowego trypsyny.