Fabrication and Characterization of Photochromic Spirooxazine/Polyvinylidene Fluoride Fiber Membranes via Electrospinning

In this study, photochromic spirooxazine material of N-methyl-3,3-dimethyl-9'-hydroxy-spiro[2H-indole-2-[3H] naphtho [2,1-b] [1,4] oxazine] was synthesised. Spirooxazine/PVDF fiber (SPF) membranes with different contents ofspirooxazine were successfully prepared by electrospinning. The SPF membranes were characterised by FTIR and SEM.The photochromic properties and contact angle of the SPF membranes were evaluated. The results show that the SPF membranes change from colorless to blue whenexposed to UV light, but they revert to their original colour after the UV light disappears. The colour difference and contact angle of the SPF membranes firstly increase and then decrease with a rise in the content of spirooxazine.

W pracy otrzymano fotochromowy materiał spirooksazynowy N-metylo-3,3-dimetylo-9'-hydroksy-spiro [2H-indolo-2 - [3H] nafto [2,1-b] [1,4] oksazyny]. Za pomocą elektroprzędzenia wytworzono membrany z spiroksaksyny i fluorku poliwalildanu PVDF (SPF) o różnej zawartości spiroksaksyny. Błony SPF scharakteryzowano za pomocą FTIR i SEM. Oceniono właściwości fotochromowe i kąt zwilżania błon SPF. Wyniki pokazały, że membrany SPF zmieniają kolor z bezbarwnego na niebieski po ekspozycji na światło UV, ale powracają do swojego pierwotnego koloru po zaniku światła UV. Różnica barwy i kąt zwilżania membran SPF najpierw wzrastają, a następnie zmniejszają się wraz ze wzrostem zawartości spirooksazyny.