Waste poly(methylene methacrylate) as precursor for activated carbons

The evaluation of the possibilities to use of waste poly(methylene methacrylate) (PMMA) in acomposition with coal-tar pitch (CTP) for the preparation of activated carbons was carried out. The polymer-pitch compositions (PMMA-CTP), containing from 10 to 50 wt % of waste PMMA were homogenized at 270 °C, for 1 hour. PMMA-CTP compositions were carbonized and activated with steam, carbon dioxide or potassium hydroxide. It was found that the activated carbon obtained from the composition containing 50 wt % of waste PMMA in the activation process with KOH was characterized by the highest iodine number (IN = 2260 mg/g), methylene blue number (MB = 33 cm³), specific surface area (BET= 3134 m²/g), micropores (1.033 cm³/g) and mesopores (0.160 cm³/g) volume.

Przedstawiono wyniki badań dotyczących wykorzystania odpadowego poli(metakrylanu metylu) (PMMA) w mieszaninie z pakiem węglowym (CTP) do otrzymywania węgli aktywnych. Kompozycje polimerowo-pakowe (PMMA-CTP), zawierające od 10 % mas. do 50 % mas. odpadu PMMA, sporządzano w temp. 270 °C w ciągu 1 godz., a następnie poddano karbonizacji i aktywacji parą wodną, ditlenkiem węgla lub wodorotlenkiem potasu. Stwierdzono, że największą liczbą jodową (IN=2260 mg/g), liczbą metylenową (MB = 33 cm³), powierzchnią właściwą (BET = 3134 m²/g) oraz objętością mikroporów (1,033 cm³/g) i mezoporów (0,160 cm³/g) charakteryzował się węgiel aktywny otrzymany z kompozycji zawierającej 50 % mas. odpadu PMMA w procesie aktywacji KOH.