Fabrication of Titanium dioxide nanotube photo-electrodes in different electrolyte mixtures and the impacts on their characteristics and photo-catalytic abilities under visible light
Fabrication of Titanium dioxide nanotube photo-electrodes in different electrolyte mixtures and the impacts on their characteristics and photo-catalytic abilities under visible light
TiO2 nanotube arrays were fabricated using electrochemical anodization of titanium foils, where different types of electrolytes were tested to determine conceptual choice for nanotubes fabrication. These electrolytes are 1M (NH4)2SO4 containing 0.5% wt NH4F, 1M Na2SO4 containing 0.5% wt NH4F, 1M NaF containing 0.5% wt (NH4)2SO4 and a mixture of water: ethylene glycol 1:9 containing 0.5% wt NH4F. The foils were marked as EG type (Ethylene Glycol), AS type (Ammonium sulfate), SS type (sodium sulfate) and SF type (sodium fluoride). The photocatalytic capabilities and characterization of the fabricated NTAs were analyzed using SEM, XRD, and DRS. The degradation ratio of designated organic pollutants (Rhodamine B) was analyzed. The obtained results have proven that foils fabricated using Ethylene glycol have significant photocatalytic abilities, with a degradation ratio of EG-SS-SF-AS types being 80% to 85%, 70% to 80%, 70% to 75% and 52% to 55%, respectively.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00