N,N-dihydroxybenzene-1,3-dicarboximidoyl dichloride was synthesized from benzene-1,3-dicarboxaldehyde and characterized
by fourier transform infrared spectroscopy (FT-IR) and nuclear magnetic resonance 1H and 13C NMR).
The elastomer was prepared through the 1,3-dipolar cycloaddition of reaction between liquid polybutadiene (LPB)
and isophthalonitrile oxide in this work. The tensile strength of different elastomer was enhanced from 0.14 MPa
to 0.33 MPa as the elongation at break decreased from 145% to 73%, and the modulus increased from 0.09 kPa
to 0.47 kPa. The parameters of kinetic indicated that the curing reaction was first order reaction and the apparent
activation energy of each curing system was less than 10.10 kJ/mol when the content of N,N-dihydroxybenzene-1,3-
dicarboximidoyl dichloride was increased from 7% to 12%. These results suggested that nitrile oxides achieved
curing of polymer binders at room temperature and this work had definite guiding significance for the application
of nitrile oxides in polymer binders.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00