The present study investigated the effect of the surface functional groups of nanosilica on the interfacial, crystallization, and thermal stability of polyamide 6/SiO2 (PA6/SiO2) nanocomposite, in which nanosilica was modified in situ with both 3-triethoxysilylpropylamine and 3-methacryloxypropyltrimethoxy silane¬ (KH-550 and KH-570). The FTIR analysis results showed the chemical bonding action between the reacting amino groups of nanosilica and end carboxyl groups of polyamide 6 enhanced with increasing the ratio of KH-550 and KH-570. The XRD spectrum indicated that the crystal structure of PA6/SiO2 nanocomposites tended to form α crystal type that was beneficial to an improvement of mechanical properties, and which was in agreement with the results of mechanical strength measurements. It was also found that crystallization temperature and crystallization rate of PA6/SiO2 nanocomposites were lower than that of neat polyamide 6.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00