In the first research studies series a selection of the quantitative composition of catalyst active phase composition (iron, copper and manganese) deposited on mineral-carbon support was carried out. It was found on the basis of the selection studies series that the best results were attained when copper and manganese were used as catalyst components. The quantitative composition of the denitrogention catalyst was estimated using a statistical method of experiment planning and metals content changed in the range 0.5 - 1.5wt % for both metals. Catalyst activity in nitric oxide reduction by ammonia was determined in the dependence on an active phase composition in the temperature range 100 - 200° C, at GHSV (Gas Hour Space Velocity) 6 000 and 10 000 Nm3/m3h, NO concentration 400 ppm, NH3/NO ratio 1:1. A graphic presentation of the obtained results was made using the UNIPLOT program. The highest activity in nitric oxide reduction by ammonia presented copper - manganese catalysts prepared by the impregnation of mineral-carbon support with active metals salts solutions and calcination after each metal impregnation with copper (up to 1.5 wt %) and manganese (up to 1.5 wt %).
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00