Plasticity and swell-shrink behaviour of electrokinetically stabilized virgin expansive soil using calcium hydroxide and calcium chloride solutions as cationic fluids

This investigation focussed on the plasticity and swell-shrink behaviour of an expansive soil that was stabilized using electro kinetic stabilization (EKS) techniques with cationic fluids for enhancement of stabilization. 0.25 M solutions of calcium hydroxide and calcium chloride were used as cationic fluids. An electro kinetic (EK) cell of dimensions 500 mm x 150 mm x 160 mm with inert graphite electrodes of size 140 mm x 160 mm x 5 mm was adopted for the stabilization process, carried out at an applied voltage of 40 V over a period of 6 hours. After the duration of the test, stabilized soil sample was subjected to Atterberg limits and free swell tests to determine its plasticity and swell-shrink characteristics. The results of the investigation found that both fluids were capable of reducing the plasticity and swell-shrink behaviour of the soil with different levels of effectiveness.

W badaniach skupiono się na plastyczności i kurczeniu się gleby, która została ustabilizowana za pomocą technik stabilizacji elektrokinetycznej (EKS) z płynami kationowymi. Jako płyny kationowe stosowano 0,25 M roztwory wodorotlenku wapnia i chlorku wapnia. Do procesu stabilizacji przyjęto ogniwo elektrokinetyczne (EK) o wymiarach 500 mm x 150 mm x 160 mm z obojętnymi elektrodami grafitowymi o wymiarach 140 mm x 160 mm x 5 mm, przy zastosowaniu napięcia 40 V przez okres 6 godzin. Po zakończeniu testu stabilizowaną próbkę gleby poddano testom Atterberga i badaniom swobodnego spęcznienia w celu określenia jego plastyczności i charakterystyki kurczenia się. Wyniki badania wykazały, że oba płyny były w stanie zmniejszyć plastyczność i kurczenie się gleby przy różnych poziomach skuteczności.