Sintered ferrous components were coated with electrochemical chromium coatings modified with nanodiamond particles. The nanodiamond particles were produced by detonation synthesis with an average grain size 8 nm. The objective of this study was to determine the tribological properties and the corrosion resistance of sintered iron samples coated with an electrochemically deposited chromium layer modified with nanodiamond particles. The thickness of the obtained composite coatings was more than 25 μm. The microstructure and microhardness were determined by metallographic methods. The mechanical and chemical properties of the samples were compared to uncoated samples prepared from the same iron powder. The microhardness was 5 times higher, the wear resistance increased 6 times and the corrosion resistance in 0.1 M NaCl solution was
10 times higher.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00