Microstructural characterization of Inconel 713C superalloy after creep testing

The main aim of this investigation was to determine the microstructural degradation of Inconel 713C superalloy during creep at high homologous temperature. The alloy in as cast condition was characterized by large microstructural heterogeneity. Inside equiaxed grains dendrite cores consisted of γ' precipitates surrounded by channels of matrix, whereas enrichment of interdendritic spaces in carbide formers, Zr and B resulted in the formation of additional constituents, namely M₃B₂, Ni₇Zr₂ and eutectic island γ/γ'. Directional coarsening of γ′ precipitates (rafting) under applied stress and decomposition of primary MC- type carbides accompanied by the formation of secondary carbides enriched in Cr and γ' phase was observed.

Głównym celem badania było określenie degradacji mikrostruktury nadstopu Inconel 713C zachodzącej podczas badania pełzania w wysokiej temperaturze homologicznej. Badany nadstop bezpośrednio w stanie lanym charaktery- zuje się wysoką niejednorodnością mikrostrukturalną. Wewnątrz ziaren równoosiowych rdzenie dendrytów składają się z wydzieleń γ' otoczonych kanałami osnowy, natomiast wzbogacenie przestrzeni międzydendrytycznych w pier- wiastki węglikotwórcze, a także Zr i B, prowadzi do tworze- nia dodatkowych składników, mianowicie eutektyki γ/γ', wę- glików MC, borków M₃B₂ oraz fazy międzymetalicznej Ni₇Zr₂. W trakcie pełzania przy parametrach T = 982ºC i naprężeniu σ = 152 MPa zaobserwowano rafting typu N fazy międzymetalicznej γ'. W przestrzeniach międzydendrytycznych w wyniku częściowego rozpuszczenia węglików typu MC wydzieliły się węgliki M₂₃C₆ bogate w Cr.