This paper presents the microstructural and fractographic analysis of damage in carbon/epoxy composites after static and fatigue strength (shear) tests at elevated temperature. The microstructural tests and fractographic analysis confirmed the complexity of degradation process and degradation mechanisms in composite structure. Multiple cracks, delaminations and interface degradation between fibre and matrix have been observed. The fracture analysis indicate the occurrence of characteristic failure area: matrix river lines, matrix rollers, fractures and reinforcing fibres imprints. The interface, except of the type of components and their features, is the principal factor determining the properties of composite material. The quality of the bonding between the reinforcing phase and matrix, mechanism of composite cracking as a whole as well as cracks of individual components are directly affected by the interface.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00