This paper describes a case study summarising the failure analysis of a stainless steel femoral stem, which failed prematurely within 36 months of exploitation in human body. In order to determine the mechanism of failure, a broken stem component were analyzed by means of macroscopic and microscopic obserwations and hardness measurements. Metallurgical obserwations revealed that the tested material does fulfill ASTM requirements. Scanning electron microscopy images revealed the presence of stress-induced cracking. The results of the hardness revealed significant nonuniformity from the surface towards the inner part of the stem. It is assumed that any discontinuity or defect on the fracture surface of the stem acted as preferential site for a crack nucleation and propagation by fatigue until the cross section of stem was not able to sustain a load generated by a patient.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00