This paper describes the possibility of using very short periods of solution annealing in the heat treatment of unmodified hypoeutectic silumin alloy AlSi7Mg0,3 casted by method of casting with crystallization under pressure with forced convection (direct squeeze casting process). Castings prepared at different casting parameters were subjected to special heat treatment called SST (Silicon Spheroidization Treatment), which were originally used only for the modified silumin alloys to spheroidization of eutectic silicon. Temperature holding time in solution annealing of T6 heat treatment is limited in the SST process to only a few minutes. It was studied the effect of casting parameters and periods of solution annealing on ultimate strength, yield strength, and especially ductility that in the unmodified silumin alloy castings is relatively low.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00