Analysis of Spent Moulding Sands with Binders of Various Thermal Degradations, in an Aspect of a Possibility of a Directional Mould Degassing

Tytuł:
Analysis of Spent Moulding Sands with Binders of Various Thermal Degradations, in an Aspect of a Possibility of a Directional Mould Degassing
Autorzy:
Łucarz, M.
Powiązania:
https://bibliotekanauki.pl/articles/380900.pdf
Data publikacji:
2016
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
moulding sand
thermal analysis
organic binder
degassing
ignition loss
masa formierska
analiza termiczna
spoiwo organiczne
odgazowanie
Źródło:
Archives of Foundry Engineering; 2016, 16, 2; 21-26
1897-3310
2299-2944
Język:
angielski
Prawa:
CC BY-NC-ND: Creative Commons Uznanie autorstwa - Użycie niekomercyjne - Bez utworów zależnych 3.0 PL
Dostawca treści:
Biblioteka Nauki
Artykuł
  Przejdź do źródła  Link otwiera się w nowym oknie
The results of investigations of spent moulding sands taken from the mould in which the metal core cooling system - to increase the cooling rate of the ladle casting - was applied, are presented in the hereby paper. The changes of the spent moulding sand at the casting external side being the result of degradation and destruction processes of organic binder, were analysed in this publication. Since the reclaimed material, obtained as a result of the mechanical reclamation of spent sands of the same type, is used as a grain matrix of the moulding sand, the amount of a binder left from the previous technological cycle is essential for the sound castings production. On the bases of investigations of the thermal analysis, ignition losses, dusts contents and pH values of the samples taken from the spent sand the conditions under which the process of gases displacing in the casting mould was realised as well as factors limiting the efficient mould degassing - were considered in this study. The possible reason of a periodical occurrence of an increased number of casting defects due to changing gas volume emission, being the reason of the realised technological process, was indicated.

Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies