This article presents measurements of the thickness of alcohol-based coatings on sand foundry cores and moulds. These coatings were applied using two methods, the dipping method and the painting method. For the purposes of the study, a zircon alcohol-based coating was prepared with three different levels of nominal viscosity; very thin at 10s, average at 20s, and thick at 30s. The coating was applied to a core made of quartz sand and furan resin. The cores were made of sand with three different grain sizes; dL = 0.22 mm – fine sand, dL = 0.33 mm medium sand, and dL = 0.47 mm coarse sand. In the study, the thickness of the coating obtained to the core was measured immediately after application as well as after drying. Additionally, the extent of penetration into the intergranular spaces of the core matrix was measured. On the basis of this study, the impact of the grain size of the core matrix on the thickness of the coating and its penetration into the core was assessed. The thickness of coatings obtained using different application methods was also assessed.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00