Characteristics of Plasticity of Hot Deformed Cu-Ti Alloys

In the paper, results of a study on the effects of deformation conditions (temperature, strain and strain rate) on flow curves, maximum flow stress and corresponding deformation of Cu-Ti alloys with various Ti contents, subjected to hot deformation, are presented. Evaluation of formability of alloys was performed with the use of a Gleeble HDS-V40 thermal-mechanical simulator during uniaxial hot compression at 700 to 900°C, strain rate of 0.1 to 10.0 s^-1 and strain of 0 to 1.2 (70%). It was found that within the analysed ranges of temperature, strain rate and strain, Cu-Ti alloys underwent uniform deformation without cracking. The largest deformation resistances were observed for the alloys with the highest Ti contents; their decrease was possible with the temperature raise and the strain rate reduction.

W pracy przedstawiono wyniki badan wpływu warunków odkształcenia (temperatura, wielkosc i predkosc odkształcenia) na przebieg krzywych płyniecia, wartosc maksymalnego naprezenia uplastyczniajacego i odpowiadajacego mu odkształcenia odkształcanych plastycznie na goraco stopów Cu-Ti o zróznicowanej zawartosci Ti. Ocene podatnosci do kształtowania plastycznego stopów przeprowadzono na symulatorze cieplno-mechanicznym systemu Gleeble HDS-V40 w warunkach jednoosiowego sciskania na goraco w zakresie temperatury od 700 do 900°C, predkosci odkształcenia od 0.1 do 10.0 s^-1 i odkształcenia od 0 do 1.2 (70%). Stwierdzono, ze w analizowanych przedziałach temperatury, predkosci i wielkosci odkształcenia stopy Cu-Ti odkształcaja sie w sposób jednorodny bez udziału pekania. Wykazano, ze najwieksze opory kształtowania plastycznego towarzysza stopom o najwyzszej zawartosci Ti, a ich zmniejszenie jest mozliwe poprzez podwyzszenie temperatury i obnizenie predkosci odkształcenia.