Impact of a Structure on Durability of Modified Nickel-Base Superalloys in Creep Conditions

The study assesses the impact of surface and bulk modification and filtration during pouring on a durability under accelerated creep conditions of casts made of IN-713C and MAR-247 nickel superalloys scrap used for manufacturing of aircraft engine parts. The impact of solutionizing (1185°C/2 h) with subsequent ageing (870°C/20 h) on the creep resistance of a casting made from MAR-247 coarse-grained superalloy was also examined. Morphological structure parameters were determined with the use of Met-Ilo software. Macrostructure analysis of casts showed very significant impact of surface modification treatment. Creep test results clearly showed that coarse grained samples of IN-713C and MAR-247 superalloys have higher creep resistance. Moreover alloy MAR-247 had higher creep durability after heat treatment compared to as-cast state.

W pracy przeprowadzono ocenę wpływu zabiegów modyfikacji powierzchniowej i objętościowej oraz filtracji podczas zalewania form na trwałość w warunkach przyspieszonego pełzania odlewów wykonanych z odpadów poprodukcyjnych nadstopów niklu IN-713C i MAR-247 stosowanych na łopatki turbin silników lotniczych. Analizie poddano również wpływ operacji przesycania (1185°C/20 h) z następnym starzeniem (870°C/20 h) na trwałość pełzaniowa odlewu wytworzonego z stopu MAR-247 o strukturze gruboziarnistej. Badania makrostruktury wykonanych odlewów wykazały bardzo istotny wpływ zabiegu modyfikowania powierzchniowego. Stosując program Met-Ilo określono istotne z punktu widzenia trwałości parametry morfologiczne struktury. Próby pełzania wskazuje, że nadstopy IN-713C i MAR-247 charakteryzujace się wiekszym makroziarnem wykazywały dłuższy czas do zerwania próbki. Ponadto próbki stopu MAR-247 poddane obróbce cieplnej wykazują większą odporność na pełzanie niż próbki w stanie lanym.