Corrosion Resistance Of Electroless Ni-P/Cu/Ni-P Multilayer Coatings

Ni-P/Cu/Ni-P multilayer coatings were prepared by deposition of Cu layer between two Ni–P layers. The Cu layer was deposited by metal displacement reaction between Cu²⁺ and Fe atoms. Corrosion behavior of single-layer Ni-P coatings, double-layer Ni-P/Cu coatings, and three-layer Ni-P/Cu/Ni-P coatings were investigated by electrochemical tests in 3.5% NaCl solution. The three-layer coatings exhibited more positive E_corr and decreased I_corr compared with conventional single-layer Ni-P coatings, which indicated an improved corrosion resistance. The polarization curves of the three-layer coatings were characterized by two passive regions. The improved corrosion resistance was not only attributed to the function of the blocked pores of Cu. The Cu interlayer also acted as a sacrificial layer instead of a barrier in the coatings, which altered the corrosion mechanism and further improved the corrosion resistance of the coatings.

Wielowarstwowe powłoki Ni-P/Cu/Ni-P wytworzono metodą osadzania miedzi pomiędzy dwoma warstwami Ni-P. Warstwę Cu otrzymano dzięki reakcji wypierania metalu przez metal (dla miedzi i żelaza). Aby określić właściwości korozyjne jednowarstwowej powłoki Ni-P, dwuwarstwowej Ni-P/Cu oraz trójwarstwowej Ni-P/Cu/Ni-P przeprowadzono pomiary elektrochemiczne w 3,5% roztworze NaCl. Powłoki trójwarstwowe w porównaniu do jednowarstwowych wykazały się większą wartością E_corr, przy malejącej wartości I_corr. Wskazuje to na poprawę odporności na korozję. Krzywe polaryzacji dla powłok trójwarstwowych charakteryzują się występowaniem dwóch obszarów pasywacji. Poprawa odporności na korozję jest skutkiem nie tylko tzw. zjawiska blokowania porów w miedzi. Powłoka z Cu działała także jako warstwa protektorowa, modyfikując mechanizm korozji i poprawiając odporność korozyjną powłok.