DSC Analysis of Order–Disorder Transition in Ni3Al Based Alloys From Ni-Al-Cr System

Ni-Al-Cr system is significant for industrial alloys based on intermetallic phase Ni3Al, that crystallizes in crystal lattice L12. It is indicated as γ′, contrary to disordered phase γ which occurs with addition of chromium. DSC analysis was performed on alloys of chemical composition from Ni75Al25÷Ni75Cr25 range of Ni-rich part of Ni-Al-Cr system. In addition, few measurements were conducted using DTA method. Based on curves registered, it was possible to identify characteristic temperature during heating and cooling of the sample. It corresponds to existence of phase boundary γ′+γ / γ in examined alloys. Results of thermal analysis were compared with results obtained with other method performed by authors which is solution calorimetric method.

Układ Ni-Al-Cr jest ważnym układem dla przemysłowych stopów na osnowie fazy międzymetalicznej Ni3Al, która krystalizuje w uporządkowanej sieci L12. Oznacza się ją jako γ′ w odróżnieniu od fazy nieuporządkowanej γ, która pojawia się wraz z dodatkiem stopowym chromu. Wykonano serię stopów, których skład chemiczny leży na linii Ni75Al25÷Ni75Cr25 w bogatej w nikiel części układu Ni-Al-Cr i poddano je analizie DSC. Dodatkowo wykonano kilka pomiarów metodą DTA. Na podstawie zarejestrowanych krzywych udało się zidentyfikować charakterystyczne temperatury podczas nagrzewania i studzenia próbki. Odpowiadają one miejscom występowania granicy międzyfazowej γ′+γ / γ w stopach. Wyniki analiz termicznych zestawiono z wynikami innej metody zastosowanej przez autorów tj. kalorymetrycznej metody typu rozpuszczania.