UV-Induced Anisotropy in CdBr2-CdBr2: Cu Nanostructures

We have found an occurrence of anisotropy in the nanostructure CdBr₂-CdBr₂: Cu nanocrystalline films. The film thickness was varied from 4 nm up to 80 nm. The films were prepared by successive deposition of the novel layers onto the basic nanocrystals. The detection of anisotropy was performed by occurrence of anisotropy in the polarized light at 633 nm He-Ne laser wavelength. The occurrence of anisotropy was substantially dependent on the film thickness and the photoinduced power density. Possible mechanisms of the observed phenomena are discussed.

Wykryto pojawienie się anizotropii w nanostrukturalnych warstwach nanokrystalicznych CdBr₂-CdBr₂: Cu. Grubość warstwy zmieniano w zakresie od 4 nm do 80 nm. Nanostrukturalne warstwy otrzymano poprzez kolejne osadzanie na nowych warstwach na podstawie nanokrystalitów. Detekcję anizotropii wykonano w spolaryzowanym świetle lasera gazowego He-Ne o długości fali 633 nm. Anizotropia optyczna występująca w warstwach w znacznym stopniu zależy od grubości warstwy i gęstości mocy indukowanej światłem. Omówiono możliwe mechanizmy obserwowanego zjawiska.