The effect of cobalt aluminate inoculant addition and melt-pouring temperature on the structure and mechanical properties of Ni-based superalloy was studied. The first major move to control the quality of investment cast blades and vanes was the control
of grain size. Cobalt aluminate (CoAl2 O4 ) is the most frequently utilized inoculant in the lost-wax casting process of Ni-based
superalloys. The inoculant in the prime coat of moulds and pouring temperature play a significant role in grain size control. The
finest surface grains were obtained when the internal surface of shell mould was coated with cobalt aluminate and subsequently
pouring was at 1480°C. The influence of selected casting parameters and inoculant addition on mechanical properties was investigated
on the basis of tensile, creep and hardness testing. The effect of grain refinement on mechanical properties were consistent
with established theories. Tests conducted at ambient temperature indicated a beneficial effect of grain refinement both on tensile
strength and hardness. In contrast at elevated temperature during creep, the reverse trend was observed.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00