Aluminium AlMg1SiCu Matrix Composite Materials Reinforced with Halloysite Particles

In this work selected results of investigations of the new AlMg1SiCu matrix composite materials reinforced with halloysite particles manufactured by powder metallurgy techniques including mechanical alloying and hot extrusion are present. The composite materials obtained as a result of mechanical synthesis and hot extrusion are characterized with the structure of evenly distributed, disperse reinforcing phase particles in fine-grain matrix of AlMg1SiCu alloy, facilitate the obtainment of higher values of strength properties, compared to the initial alloy. The nanostructural composite materials reinforced with halloysite nanotubes with 15 mass % share are characterized by almost twice as higher micro-hardness - compared to the matrix material.

W pracy przedstawiono wybrane wyniki badań materiałów kompozytowych o osnowie stopu AlMg1SiCu wzmacnianych cząstkami hałoizytowymi wytworzonymi z wykorzystaniem metod metalurgii proszków, w tym mechanicznej syntezy i wyciskania na gorąco. Otrzymane w procesie mechanicznej syntezy i wyciskania na gorąco materiały kompozytowe charakteryzują się strukturą równomiernie rozłożonych, rozdrobnionych cząstek fazy wzmacniającej w drobnoziarnistej osnowie stopu AlMg1SiCu, sprzyjającą osiąganiu wyższych wartości właściwości wytrzymałościowych w porównaniu do stopu wyjściowego. Wytworzone nanostrukturalne materiały kompozytowe wzmacniane nanorurkami hałoizytowymi o udziale masowym 15% charakteryzują się - w porównaniu do materiału osnowy - ponad dwukrotnie większą mikrotwardością.