In this paper, fabrication of open-celled porous Fe-10%A1 foam by space-holder technique in which NaCl powder and polyester resin were utilized as space holder and binder respectively to generate 30-80% porosities was studied. FeAl solid solution was prepared via mechanical alloying method after 25 h high energy milling process. The results indicate that the size and shapes of the pores are determined by the size and shapes of NaCl particles. Also, when compaction pressure was in the range of 70-150 MPa and the sintering process was performed at temperature around 1100°C, the samples had the best quality. Microstructure observations show the pore size was in the range of 200-500 μm.
W niniejszej pracy badano wytwarzanie techniką wypełniacza przestrzeni piany Fe-10%Al o otwartej porowatości, w której proszek NaCl i Żywicę poliestrową wykorzystano odpowiednio w roli wypełniacza porów i spoiwa do wytworzenia piany o 30-80% porowatości. Roztwór stały FeAl został wytworzony poprzez mechaniczne stopowanie przez 25 h w trakcie wysokoenergetycznego mielenia. Wyniki wskazują, że rozmiar i kształt porów determinowany jest przez wielkość i kształt cząstek NaCl. Ponadto, gdy ciśnienie prasowania było w zakresie 70-150 MPa a proces spiekania prowadzono w temperaturze około 1100°C. próbki miały najwyższą jakość. Obserwacje mikrostruktury wykazały, że rozmiar porów mieścił się w zakresie 200-500 μm.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00