Effects of solution treatment on room temperature mechanical properties were studied in cast AZ91 (Mg-9%Al-1%Zn-0.2%Mn)
and AZ91-0.5%Ca alloys. In as-cast state, the Ca addition contributed to the suppression of discontinuous β phase precipitation
and the formation of Al2 Ca phase. After solution treatment, the AZ91 alloy had only a small amount of Al8 Mn5 particles, while
β and Al2 Ca phases were still present in the Ca-containing alloy. In as-cast state, the AZ91-0.5%Ca alloy showed better yield
strength and hardness than the AZ91 alloy. The solution treatment increased the elongation in both alloys, which eventually led
to the increase in ultimate tensile strength. The solution treatment resulted in a marked decrease in yield strength and hardness in
the AZ91 alloy, whereas the decrements in those values were relatively negligible in the Ca-containing alloy due to the residual
phases and solution hardening effect of Ca.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE W OKRESIE WAKACYJNYM BIBLIOTEKA BĘDZIE FUNKCJONOWAŁA W ZMIENIONYCH GODZINACH::
od 15 do 31 lipca:
Wypożyczalnia i Czytelnia Główna:
9.00 - 15.00
(poniedziałek-piątek)
Czytelnia Działu Zbiorów Specjalnych:
9.00 - 15.00
(poniedziałek-piątek)
od 1 do 31 sierpnia:
BIBLIOTEKA BĘDZIE NIECZYNNA
UWAGA:
Zwrotu wypożyczonych materiałów można dokonać u dyżurującego bibliotekarza w Wypożyczalni Głównej od 9.00 do 15.00.
Na pozycje, których termin zwrotu przypadnie od 1 do 31 sierpnia, wprowadzona zostanie prolongata (nowy termin zwrotu – 6 września).