Gelcasting of alumina with application of new monomer synthesised from xylitol

A new monomer for application in the gelcasting process has been designed and synthesized, following the green chemistry trend to use non toxic and renewable compounds. Xylitol was the main substrate for the synthesis that included 3 stages. The final product, named 1-O-acryloylxylitol, was tested regarding its effectiveness as the processing agent for fabrication of alumina elements by gelcasting method. Rheological properties of the ceramic slurries were studied as well as the properties of shaped elements before and after sintering. The results are compared to those obtained by applying commercial monomer 2-hydroxyethyl acrylate.

Podążając za trendem „zielonej chemii", zakładającym m.in. wykorzystywanie nietoksycznych i odnawialnych surowców w technologii, zaprojektowano i zsyntezowano nowy monomer przeznaczony do zastosowania w procesie odlewania żelowego. Wyjściowym substratem trójetapowej syntezy był ksylitol, a finalnym produktem 1-O-akryloiloksylitol. Otrzymana pochodna została sprawdzona pod względem efektywności polimeryzacji in situ w ceramicznej masie lejnej na bazie tlenku glinu. Zbadano jej wpływ na właściwości neologiczne stosowanych zawiesin. Odlano serie kształtek, dla których wyznaczono podstawowe parametry w stanie surowym oraz po spiekaniu. Wyniki porównano stosując równolegle komercyjnie dostępny monomer akrylan 2-hydroksyetylu.