Investigations of α +β → β fhase transformation in monotonically heated Ti6Al7Nb alloy

This paper presents an evaluation of critical temperatures of α +β → βphase transformation in an Ti6Al7Nb alloy occurring during heating performed by dilatometric and metallographic methods. Also, changes in the alloy microstructure during cooling down from the two-phase (α+β) and single phase (β) ranges have been analysed. In the microstructure of the alloy quenched from temperature above 1010° C (one-phase range) in water, the very fine, needle-like precipitates (presumably α) were observed as well as abnormal grain growth of the primary β phase. The obtained results may serve for the interpretation of phase transformation occurring in the Ti6Al7Nb alloy during tempering. In future, the kinetics of the phase transformation during tempering will be investigated by original CHT (Continuous-Heating-Transformation) charts, which are commonly applied for iron-base alloys.

W artykule metodami dylatometryczna i metalograficzna określono temperatury początku i końca przemiany fazowej α+β→β przy nagrzewaniu stopu Ti6Al7Nb. Dokonano również analizy zmian twardości oraz zmian zachodzących w jego mikrostrukturze przy chłodzeniu z zakresu dwufazowego α+β i jednofazowego β . W mikrostrukturze stopu oziębianego w wodzie od temperatury powyżej 1010°: C (z zakresu jednofazowego β) ) obserwuje sie drobne, iglaste wydzielenia fazy martenzytycznej (prawdopodobnie α) oraz znaczny rozrost ziaren byłej fazy β. Uzyskane wyniki badan wstępnych stopu Ti6Al7Nb będą podstawa do interpretacji przemian fazowych zachodzących podczas jego odpuszczania. Kinetykę przemian fazowych przy odpuszczaniu zamierza się będąc w przyszłości przy pomocy oryginalnych wykresów CTPc ° (czas-temperatura-przemiana przy nagrzewaniu ciągłym ze stanu zahartowanego), wprowadzonych już do literatury światowej - jak dotychczas - tylko dla stopów na osnowie żelaza.