The present article describes selected aspects of investment casting technology for manufacturing of open-cell aluminium. The main focus is, among others, on the precursor thickening. Two groups of total 30 samples were produced, basing on open-cell polyurethane foam used as the precursor. Each of the two sample groups was thickened with a different type of suspension consisting of carbonaceous substances and organic binders. The influence of the coating mixture type was compared, leading to conclusions regarding the desired composition and fluidity of the suspensions. Both sample groups of the obtained open-cell aluminium had stochastic cell distributions, the average pore diameter was 5.2 mm and the PPI index was 8. The apparent densities were respectively: 0.485 g/cm3 and 0.312 g/cm3 , which reflected the impact of the precursor coating. Additionally, samples from both groups differed in quality.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00