Elimination of Aluminum During the Process of Ti-6Al-4V Alloy, Smelting in a Vacuum Induction Furnace

In the paper, results of the study on kinetics of aluminum evaporation from a liquid Ti-6Al-4V alloy during its smelting in a vacuum induction furnace are presented. The experiments were performed with the use of a VIM 20-50 furnace (manufactured by SECO-WARWICK) at 1973 K and 5-1000 Pa. Based on the values of changes in aluminum concentration in a liquid alloy, overall mass transfer coefficients were estimated. Within the analysed pressure range, the coefficient values changed from 0.97·10⊃ -5 ms⊃ -1 to 1.93·10⊃ -5 ms⊃ -1 for 1000 Pa and 5 Pa, respectively.

W pracy przedstawiono wyniki badan kinetyki procesu odparowania aluminium z ciekłego stopu Ti-6Al-4V w trakcie jego wytopu w próżniowy piecu indukcyjnym. Badania realizowano w piecu VIM 20-50 produkcji firmy SECO-WARWICK w temperaturze 1973 K i zakresie ciśnień 5-1000 Pa. Na podstawie uzyskanych wyników zmian stężenia aluminium w ciekłym stopie oszacowano wartości ogólnego współczynnika transportu masy. W analizowanym zakresie ciśnień wartość tego współczynnika zmieniała się odpowiednio od 0,97·10⊃ -5 ms⊃ -1 dla ciśnienia 1000 Pa do 1.93·10⊃ -5 ms⊃ -1 dla ciśnienia 5 Pa.