Synthesis Of SiC/Cu Composite Powders From Polycarbosilane And Cupric Nitrate Trihydrate Synteza kompozytowych proszków SiC/Cu z polikarbosilanu i trihydratu azotanu miedzi(II)
SiC/Cu composite powders with the barrier coating of SiC-Al onto SiC powders were synthesized from Al-containing polycarbosilane precursor and Cu-nitrate hydrate. Curing at 200°C and high temperature pyrolysis at 1600°C was used to achieve the crystallization of precursor, forming the SiC-Al coating on the surface of SiC powders. A core-shell structure with the core of SiC and the shell of Cu was constructed by calcination and hydrogen-reduction of Cu nitrate hydrate. XRD and SEM analysis revealed that the β-SiC and 4H-SiC phases were formed on the surface of the initial α-SiC powders. Also, it was observed by EDX mapping that core powders of SiC were homogeneously surrounded with the fine Cu particles on their surface.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00