Nanobainitic Structure Recognition and Characterization Using Transmission Electron Microscopy

Various transmission electron microscopy techniques were used for recognition of different kinds of bainitic structures in 100CrMnSi6-4 bearing steel. Upper and lower bainite are morphologically different, so it is possible to distinguish between them without problem. For new nanobainitic structure, there is still controversy. In studied bearing steel the bainitic ferrite surrounding the retained austenite ribbon has a high density of dislocations. Significant fragmentations of these phases occur, bainitic ferrite is divided to subgrains and austenitic ribbons are curved due to stress accommodation.

W celu rozpoznania i scharakteryzowania poszczególnych morfologii bainitycznych w stali łożyskowej 100CrMnSi6-4 zastosowano różne techniki transmisyjnej mikroskopii elektronowej. Rozpoznawanie bainitu górnego i dolnego nie nastręcza problemu, ze względu na ich zróżnicowane morfologie. W przypadku bezwęglikowego nanobainitu, ciagle jeszcze wiele jest kontrowersji. W badanej stali łożyskowej ferryt bainityczny otaczający wstęgi austenitu szczątkowego cechuje się dużą gęstością dyslokacji. Obydwie fazy wykazują znaczną fragmentacje; ferryt bainityczny podzielony jest na podziarna a wstążki austenitu ulegaja wygięciu w wyniku akomodacji naprężeń.