Effect of Heat Treatment Parameters on the Formation of ADI Microstructure with Additions of Ni, Cu, Mo

Metallographic examinations and mechanical tests were carried out on the ductile iron with additions of Ni, Cu and Mo in as-cast state and after austempering. TTT and CCT diagrams were plotted. The heat treatment was performed in six different variants. Studies included qualitative assessment of the microstructure and testing of mechanical properties such as R_0,2, R_m, A, Z, HRC, KC. An analysis of the obtained results was also presented.

Przeprowadzono badania metaloznawcze żeliwa sferoidalnego z dodatkami Ni, Cu i Mo w stanie lanym i po hartowaniu izotermicznym. Opracowano wykresy CTPi i CTPc. Obróbkę cieplną wykonano w sześciu różnych wariantach. Badania metaloznawcze obejmowały ocenę jakościową mikrostruktury i pomiary właściwości mechanicznych: R_0,2, R_m, A, Z, HRC, KC. Dokonano analizy uzyskanych wyników