We investigated the effect of pre-sintering process on the penetration behavior of Dy in a NdFeB sintered magnet which was grain boundary diffusion treated with Cu/Al mixed Dy source. The pre-sintering of a magnet was performed at 900°C in vacuum and
then the pre-sintered body was dipped in the solutions of DyH2, DyH2 + Cu, and DyH2 + Al, respectively. The dipped pre-sintered
body were then fully sintered 4 hours at 1060°C followed by a subsequent annealing. The pre-sintering apparently improved the
diffusivity of Dy atoms. The penetration of Dy into the magnet extended almost to 2,000 μm from the surface, about four times
deeper than that of the normally sintered and diffusion treated one, when the DyH2 + Al solution was used as a Dy source. However,
the resulting increase of coercivity was about 4 kOe, somewhat lower than that of the normally treated one, mostly due to excessive
oxide formation that hindered to make a continuous Nd-rich grain boundary phase and a core-shell type structure.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00