The aim of this study was to assess the quality of the passive layer formed on the surface of a CoCr alloy used on dentures to see the effect on resistance to pitting corrosion and electrochemical parameters. Studies were performed using on potentiodynamic tests and electrochemical impedance spectroscopy. The passive layer was formed spontaneously and by electrochemical method on samples after casting and after simulation porcelain firing on metal. Samples of the passivation electrochemical characterized by the improvement in corrosion resistance. Prolonging the passivation time from one to 24 hours and increasing the potential value from 0 to 200 mV improved the quality of the passive layer and all characteristics of electrochemical parameters.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00